Interface structure and mechanical properties of the brazed joint of TiC cermet and steel

被引：26

作者：

Feng, JC ^{[1
]}

Zhang, LX ^{[1
]}

机构：

[1] Harbin Inst Technol, Natl Key Lab Adv Welding Proc Technol, Harbin 150001, Peoples R China

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2006年 / 26卷 / 07期

基金：

中国国家自然科学基金;

关键词：

TiC cermet; joining; interfaces; microstructure; strength;

D O I：

10.1016/j.jeurceramsoc.2005.01.043

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A commercially available Ag-Cu braze alloy foil with Zn Was Used to join TiC cermet and steel. According to the experimental observations, the interface structure is (Cu, Ni)/Ag (s.s.) + Cu (s.s.)/(Cu, Ni)/(Cu, Ni) + (Fe Ni) from TiC cermet to steel side. With increased brazing temperature or time, the amounts of (Cu, Ni) near the base metals/Ag-31Cu-23Zn interface and (Cu, Ni) + (Fe, Ni) near the Ag-31Cu-23Zn/steel interface increase, while the amount of Ag (s.s.) + Cu (s.s.) in the middle of the braze alloy decreases. The whole joining process consists of diffusion and solution among atoms of the braze alloy foil and base metals. The maximum shear strength is 120.7 MPa for the joint brazed at 850 degrees C for 10 min. (c) 2005 Elsevier Ltd. All rights reserved.

引用

页码：1287 / 1292

页数：6

共 50 条

[1] Interface structure and bonding strength of brazed joint of TiC cermet/steel
Feng, Ji-Cai
Jing, Xiang-Meng
Zhang, Li-Xia
Liu, Hong
Hanjie Xuebao/Transactions of the China Welding Institution, 2006, 27 (01): : 5 - 8
[2] Interfacial Microstructure and Mechanical Properties of TiC-Ni Cermet Joint Brazed with Ag-Cu28 Alloy
Zheng, Qingze
Lei, Min
Liu, Haichun
Wei, Zixiong
Li, Yulong
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2025,
[3] Interfacial Microstructure and Properties of TiC Cermet and GH3128 Joint Brazed Using AgCuNiLi
Zhang Lixia
Lei Min
Yang Zhiye
Feng Jicai
RARE METAL MATERIALS AND ENGINEERING, 2017, 46 (11) : 3410 - 3415
[4] Study on the interface microstructure and mechanical properties of 5005 aluminum alloy and stainless steel brazed joint
State Key Laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin 150001, China
Cailiao Kexue yu Gongyi, 2009, SUPPL. 1 (124-127):
[5] Dynamic mechanical and fracture properties of an infiltrated TiC-1080 steel cermet
Rittel, D
Frage, N
Dariel, MP
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2005, 42 (02) : 697 - 715
[6] Interface structure and mechanical properties of Ti(C,N)-based cermet and 17-4PH stainless steel joint brazed with nickel-base filler metal BNi-2
Wang, F. Z.
Wang, Q. Z.
Yu, B. H.
Xiao, B. L.
Ma, Z. Y.
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2011, 211 (11) : 1804 - 1809
[7] The Effect of W, Cr, Mo Content on the Microstructure and Mechanical Properties of the Weld Interface of TiC Cermet and Low-Carbon Steel
Wei, Wei
Huang, Zhiquan
Zhang, Haiyan
Guan, Shaokang
COATINGS, 2024, 14 (05)
[8] BRAZING OF TIC CERMET TO STEEL
Laansoo, A.
Kuebarsepp, J.
Vainola, V.
PROCEEDINGS OF THE 7TH INTERNATIONAL CONFERENCE OF DAAAM BALTIC INDUSTRIAL ENGINEERING, VOLS 1 AND 2, 2010, : 480 - 485
[9] Investigation on Wettability and Metallurgical and Mechanical Properties of Cemented Carbide and Steel Brazed Joint
Mousavi, S. A. A. Akbari
Sherafati, P.
Hoseinion, M. M.
MATERIALS AND MANUFACTURING TECHNOLOGIES XIV, 2012, 445 : 759 - +
[10] Numerical simulation of TiC cermet/iron joint brazed with Ag-Cu-Zn filler metal
Zhang, LX
Zhang, CP
Feng, JC
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2005, 15 : 30 - 34

← 1 2 3 4 5 →