Core structure and strengthening mechanism of the misfit dislocation in nickel-based superalloys during high-temperature and low-stress creep

被引:9
|
作者
Ma, Shiyu [1 ]
Lv, Xianzi [1 ]
Zhang, Jianxin [1 ]
Zhang, Youjian [1 ]
Li, Pan [1 ]
Jin, Huixin [1 ]
Zhang, Wenyang [1 ]
Li, Xueqiao [2 ]
Mao, Shengcheng [2 ]
机构
[1] Shandong Univ, Key Lab Liquid Solid Struct Evolut & Proc Mat, Minist Educ, Jinan 250061, Shandong, Peoples R China
[2] Beijing Univ Technol, Beijing Key Lab Microstruct & Property Adv Mat, Beijing 100024, Peoples R China
基金
中国国家自然科学基金;
关键词
Nickel based superalloys; High-temperature and low-stress creep; Misfit dislocation; Core structure; Stress distribution; Strengthening mechanism; SINGLE-CRYSTAL SUPERALLOY; NI-BASED SUPERALLOYS; INTERFACIAL DISLOCATIONS; GAMMA'-PHASE; MICROSTRUCTURE; ADDITIONS; EVOLUTION; GEOMETRY; NETWORK; MOTION;
D O I
10.1016/j.jallcom.2018.01.323
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Misfit dislocation structures are investigated in a nickel-based single crystal superalloy subjected to 38.8 h creep at 1100 degrees C and 130 MPa using conventional and high resolution transmission electron microscopy (HRTEM). The misfit dislocation was identified as an uncommon one with Burgers vector b = a/2[(2) over bar 11], which can be described as inserting (or extracting) one (1 (1) over bar1) half plane and one (11 (1) over bar) half plane. This dislocation was decomposed into two partial dislocations b(1) and b(2), with b(1) = a/2[(1) over bar 01] and b(2) = a/2[(2) over bar 11]. Partial dislocations b(1) and b(2) were arranged in a "V" shape, connected by the antiphase boundary (APB), which could hinder the dislocation motion to achieve the effect of dislocation enhancement. (c) 2018 Elsevier B.V. All rights reserved.
引用
收藏
页码:372 / 376
页数:5
相关论文
共 50 条
  • [41] Fretting fatigue damage mechanism of Nickel-based single crystal superalloys at high temperature
    Sun, Shouyi
    Li, Lei
    He, Kun
    Yue, Zhufeng
    Yang, Weizhu
    Yu, Zhiyuan
    INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 2020, 186
  • [42] MICROSTRUCTURAL DEGRADATION OF ALUMINIDE COATINGS ON SINGLE-CRYSTAL NICKEL-BASED SUPERALLOYS DURING HIGH-TEMPERATURE EXPOSURE
    GALE, WF
    KING, JE
    MATERIALS SCIENCE AND TECHNOLOGY, 1993, 9 (09) : 793 - 798
  • [43] DISLOCATION LINK LENGTH DISTRIBUTIONS IN HIGH-TEMPERATURE LOW STRESS CREEP OF ALUMINUM
    LEE, SS
    ARDELL, AJ
    JOURNAL OF METALS, 1984, 36 (07): : 62 - 62
  • [44] Internal stress and effect factors for single crystal nickel-based superalloys during steady state creep
    Tian, Sugui
    Zhang, Jinghua
    Jin, Tao
    Yang, Hongcai
    Xu, Yongbo
    Hu, Zhuangqi
    Hangkong Cailiao Xuebao/Journal of Aeronautical Materials, 1998, 18 (03): : 16 - 21
  • [45] Interactions between interfacial dislocations and / interface during high temperature - low stress creep in nickel-based single crystal superalloy
    Huang, Ming
    Yang, Xinye
    Xiong, Jichun
    Li, Jiarong
    Yang, Sen
    Qin, Yuan
    PHILOSOPHICAL MAGAZINE LETTERS, 2018, 98 (09) : 392 - 399
  • [46] Evolution of superdislocation structures during tertiary creep of a nickel-based single-crystal superalloy at high temperature and low stress
    Tang, Yuling
    Huang, Ming
    Xiong, Jichun
    Li, Jiarong
    Zhu, Jing
    ACTA MATERIALIA, 2017, 126 : 336 - 345
  • [47] Mechanisms of high temperature creep of nickel-base superalloys under low applied stress
    Epishin, A
    Link, T
    Superalloys 2004, 2004, : 137 - 143
  • [48] γ′-cutting as rate-controlling recovery process during high-temperature and low-stress creep of superalloy single crystals
    Srinivasan, R
    Eggeler, GF
    Mills, MJ
    ACTA MATERIALIA, 2000, 48 (20) : 4867 - 4878
  • [49] THE INFLUENCE OF GASEOUS IMPURITIES IN AIR ON THE HIGH-TEMPERATURE CORROSION OF COATED AND UNCOATED NICKEL-BASED SUPERALLOYS
    LINK, T
    RAHMEL, A
    SCHUTZE, M
    MATERIALS AT HIGH TEMPERATURES, 1995, 13 (01) : 55 - 66
  • [50] Influence of prestraining on the high-temperature fatigue behaviour of polycrystalline nickel-based superalloys in the VHCF range
    Stoecker, Christian
    Zimmermann, Martina
    Christ, Hans-Juergen
    FATIGUE 2010, 2010, 2 (01): : 1383 - 1392