Magnetic properties of NdMn1-xFexO3+δ system

Magnetization, AC susceptibility and specific heat measurements were performed on polycrystalline NdMn1-xFexO3+delta compounds (x = 0.0, 0.1 and 0.2). Substitution of Fe for Mn reduces the Neel temperature T-N, which is associated with magnetic ordering of Mn sublattice, from 85.5 K to 57.0 K. The temperature dependence of magnetization for x = 0.2 exhibits the compensation temperature and the pole inversion below T-comp = 26.7(5) K. Initial magnetization curves present a remnant magnetization in the ordered region with the sign of remnant magnetization depending on temperature. The substitution of Fe for Mn changes hysteresis loop of NdMnO3+delta. from the ferromagnetic- like one (mu H-0(c) = 0.09 T) by expanding the width of the loop (mu H-0(c) = 0.55 T) for x = 0.1 and then shrinking the central part of the loop to "butterfly" type (mu H-0(c) = 0.35 T) for x = 0.2.