Technical Note: Corrosion Fatigue Crack Growth of Forged Type 316NG Austenitic Stainless Steel in 325°C Water

被引：6
|
作者：
Xiao, J. [1 ]
Chen, L. Y. [1 ]
Zhou, J. [1 ]
Qiu, S. Y. [1 ]
Chen, Y. [1 ]
机构：
[1] Nucl Power Inst China, Sci & Technol Reactor Fuel & Mat Lab, Chengdu 610041, Sichuan, Peoples R China
来源：
CORROSION | 2018年 / 74卷 / 04期
关键词：
fatigue crack growth; pressurized water reactor; primary coolant pipe; Type 316NG austenitic stainless steel; LOW-CYCLE FATIGUE; TEMPERATURE; BEHAVIOR; LIFE; ENVIRONMENTS; MECHANISMS; INITIATION; DEFLECTION; PRESSURE;
D O I：
10.5006/2647
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Forged Type 316NG austenitic stainless steel is commonly used to fabricate primary coolant pipe in advanced pressurized water reactor systems, but it is subject to corrosion fatigue cracking in primary coolant environments. In this study, the fatigue crack growth of Type 316NG austenitic stainless steel in 325 degrees C water was investigated. The corrosion fatigue effect in 325 degrees C water was mainly correlated to the crack growth rate and load frequency. A maximum F-en (environment corrected factor) value up to 100 was observed at f = 0.005 Hz, Delta K = 13 MPa root m. The dissolved oxygen tended to have little influence on the fatigue crack growth. The crack path was deflected and branched. Most secondary cracks tended to be initiated from grain boundaries.
引用
收藏
页码：387 / 392
页数：6
相关论文
共 50 条
  • [31] Effect of Zinc on Stress Corrosion Crack Growth Rate of Type 316 Stainless Steel
    Du, Donghai
    Chen, Kai
    Zhang, Lefu
    Shi, Xiuqiang
    Yin, Kaiju
    Hedongli Gongcheng/Nuclear Power Engineering, 2017, 38 (02): : 78 - 83
  • [32] Effects of Corrosion Potential, Dissolved Oxygen, and Chloride on the Stress Corrosion Cracking Susceptibility of a 316NG Stainless Steel Weld Joint
    Wang, Jiamei
    Su, Haozhan
    Ajmand, Farzin
    Zhang, Lefu
    Chen, Kai
    CORROSION, 2019, 75 (08) : 946 - 959
  • [33] Fatigue behavior of Austenitic Type 316L Stainless Steel
    Mohammad, K. A.
    Ali, Aidy
    Sahari, B. B.
    Abdullah, S.
    1ST INTERNATIONAL CONFERENCE ON MECHANICAL ENGINEERING RESEARCH 2011 (ICMER2011), 2012, 36
  • [34] Corrosion fatigue crack growth behavior of 316LN stainless steel in high-temperature pressurized water
    Zhang, Ziyu
    Tan, Jibo
    Wu, Xinqiang
    Han, En-Hou
    Ke, Wei
    NUCLEAR ENGINEERING AND TECHNOLOGY, 2021, 53 (09) : 2977 - 2981
  • [35] Environmental fatigue crack growth rate of Type 347 austenitic stainless steel in simulated PWR water conditions
    Hong, Seokmin
    Min, Ki-Deuk
    Jeon, Soon-Hyeok
    Lee, Bong-Sang
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2018, 167 : 11 - 17
  • [36] IMPURITY AND STRAIN-RATE EFFECTS ON STRESS-CORROSION CRACKING BEHAVIOR OF TYPES 316NG AND 316 STAINLESS-STEEL
    MAIYA, PS
    SHACK, WJ
    JOURNAL OF METALS, 1983, 35 (08): : A39 - A39
  • [37] Stress corrosion crack initiation in machined type 316L austenitic stainless steel in simulated pressurized water reactor primary water
    Chang, Litao
    Burke, M. Grace
    Scenini, Fabio
    CORROSION SCIENCE, 2018, 138 : 54 - 65
  • [38] Fatigue and creep-fatigue crack growth in 316 stainless steel cracked plates at 650°C
    Marie, S
    Delaval, C
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2001, 78 (11-12) : 847 - 857
  • [39] The Influence of Hydrogen on Crack Initiation During Rotating Beam Fatigue Testing of Type 316 Austenitic Stainless Steel
    Matson, D. M.
    Skipper, C. O.
    Leisk, G. G.
    Saigal, A.
    TMS 2010 139TH ANNUAL MEETING & EXHIBITION - SUPPLEMENTAL PROCEEDINGS, VOL 3: GENERAL PAPER SELECTIONS, 2010, : 327 - 333
  • [40] Environmental fatigue testing of type 316 stainless steel in 310°C water
    Cho, Hyunchul
    Kim, Byoung Koo
    Kim, In Sup
    Oh, Seung Jong
    Jung, Dae Yul
    Byeon, Seong Cheol
    Proceedings of the ASME Pressure Vessels and Piping Conference - 2005, Vol 1, 2005, : 165 - 169
12345