Subcritical crack growth in Low Temperature Co-fired Ceramics under biaxial loading

被引：32
|
作者：
Bermejo, R. [1 ]
Supancic, P. [1 ,2 ]
Krautgasser, C. [2 ]
Morrell, R. [1 ,3 ]
Danzer, R. [1 ,2 ]
机构：
[1] Univ Leoben, Inst Struktur & Funkt Keram, A-8700 Leoben, Austria
[2] Mat Ctr Leoben, A-8700 Leoben, Austria
[3] Natl Phys Lab, Teddington TW11 0LW, Middx, England
来源：
ENGINEERING FRACTURE MECHANICS | 2013年 / 100卷
关键词：
Low Temperature Co-fired Ceramics; Environmentally assisted cracking; Fracture mechanics; Failure assessment; Lifetime prediction; 3 BALLS TEST; LIFETIME MEASUREMENTS; BRITTLE DISCS; STRENGTH; PROPAGATION; FRACTURE; WATER; TOUGHNESS; FLEXURE; GLASS;
D O I：
10.1016/j.engfracmech.2012.12.004
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
The biaxial strength of Low Temperature Co-fired Ceramics was determined using the ballon-three-balls test in several environments (dry oil, air and water). Subcritical crack growth phenomenon was observed, activated by the prolonged presence of humidity at the specimen surface. Whereas high strength values were reached during high-rate testing in dry oil, up to a 50% lower strength was measured on specimens immersed in water tested for longer periods. Experiments in a relative dry environment have shown for the first time evidence of two different crack growth mechanisms in this material. A model has been implemented to interpret the experimental results. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：108 / 121
页数：14
相关论文
共 50 条
  • [21] High-Temperature Joining of Low-Temperature Co-Fired Ceramics
    Walker, C. A.
    Uribe, F.
    Monroe, S. L.
    Stephens, J. J.
    Goeke, R. S.
    Hodges, V. C.
    BRAZING AND SOLDERING, PROCEEDINGS, 2006, : 54 - 59
  • [22] Impact of firing temperature on insulating properties of Low Temperature Co-fired Ceramics
    Dabrowski, Arkadiusz P.
    MATERIALS SCIENCE-POLAND, 2020, 38 (01) : 189 - 196
  • [23] Studies on laser ablation of low temperature co-fired ceramics (LTCC)
    Yung, Winco K. C.
    Zhu, Jijun
    MICROELECTRONICS INTERNATIONAL, 2007, 24 (03) : 27 - 33
  • [24] LOW TEMPERATURE CO-FIRED CERAMICS (LTCC) - DESIGN AND CHARACTERIZATION OF INTERFACES
    Rabe, Torsten
    Eberstein, Markus
    Schiller, Wolfgang A.
    CHARACTERIZATION AND CONTROL OF INTERFACES FOR HIGH QUALITY ADVANCED MATERIALS II, 2007, 198 : 173 - 178
  • [25] Electromagnetic Bandgap Structure by Low Temperature Co-fired Ceramics Technology
    Zhang Xiaoqing
    Li Bo
    Pang Xinfeng
    Sun Jingbo
    Wu Jun
    Chen Bingyang
    Guo Hai
    Zhou Ji
    Li Longtu
    APPLICATIONS OF ENGINEERING MATERIALS, PTS 1-4, 2011, 287-290 : 377 - +
  • [26] Electromagnetic Valve Made in Low-Temperature Co-Fired Ceramics
    Czok, Mateusz J.
    Malecha, Karol
    Golonka, Leszek J.
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2014, 11 (03) : 468 - 474
  • [27] Studies on laser ablation of low temperature co-fired ceramics (LTCC)
    Zhu, Jijun
    Yung, Winco K. C.
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2009, 42 (7-8): : 696 - 702
  • [28] Lifetime prediction for mechanically stressed low temperature co-fired ceramics
    Dannheim, H
    Schmid, U
    Roosen, A
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2004, 24 (08) : 2187 - 2192
  • [29] Shaped electronic substrates in low-temperature co-fired ceramics
    Lodge, KJ
    GEC JOURNAL OF TECHNOLOGY, 1998, 15 (02): : 118 - 126
  • [30] Studies on laser ablation of low temperature co-fired ceramics (LTCC)
    Jijun Zhu
    Winco K C Yung
    The International Journal of Advanced Manufacturing Technology, 2009, 42 : 696 - 702
12345