Mechanical Properties and CMAS Corrosion Resistance of La2Ce2O7/YSZ Composite Thermal Barrier Coatings

被引：0
|
作者：
Kang, Y. X. [1 ]
Bai, Y. [1 ]
Bao, C. G. [1 ]
Fan, W. [1 ]
Zhang, L. [1 ]
机构：
[1] Xi An Jiao Tong Univ, State Key Lab Mech Behav Mat, Xian 710049, Peoples R China
来源：
INTERNATIONAL THERMAL SPRAY CONFERENCE AND EXPOSITION (ITSC 2018) | 2018年
基金：
中国国家自然科学基金;
关键词：
LANTHANUM-CERIUM OXIDE; TEMPERATURE; STRESSES;
D O I：
暂无
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
50 vol. % La2Ce2O7 (LC)/yttria partially stabilized zirconia (YSZ) composite thermal barrier coating (TBC) was deposited by supersonic atmospheric plasma spraying (SAPS). The mixture of LC and YSZ can effectively eliminate the sudden decrease of thermal expansions coefficients of LC. The results of CMAS corrosion tests indicated that the LC/YSZ composite coating reveals high resistance to the penetration of CMAS with reprecipitation of La-Ce apatite, CaAl2Si2O8, MgAl2O4 and t-ZrO2. Furthermore, compared to YSZ coating, the LC/YSZ composite coating can obviously improve the thermal cycling lives under CMAS corrosion.
引用
收藏
页码：75 / 78
页数：4
相关论文
共 50 条
  • [21] Hot corrosion behavior of plasma sprayed La2Ce2O7/YSZ thermal barrier composite coating in the presence of Sulfate and Vanadate molten Salts
    Dehkharghani, Amir Mohammad Fathi
    Rahimipour, Mohammad Reza
    Zakeri, Mohammad
    CORROSION SCIENCE, 2021, 183 (183)
  • [22] Thermophysical properties of solution precursor plasma-sprayed La2Ce2O7 thermal barrier coatings
    Bei-Bei Feng
    Yi Wang
    Qiang Jia
    Wei Huang
    Hong-Li Suo
    Wen Ma
    Rare Metals, 2019, 38 : 689 - 694
  • [23] Thermophysical properties of solution precursor plasma-sprayed La2Ce2O7 thermal barrier coatings
    Feng, Bei-Bei
    Wang, Yi
    Jia, Qiang
    Huang, Wei
    Suo, Hong-Li
    Ma, Wen
    RARE METALS, 2019, 38 (07) : 689 - 694
  • [24] Thermophysical properties of solution precursor plasma-sprayed La2Ce2O7 thermal barrier coatings
    Bei-Bei Feng
    Yi Wang
    Qiang Jia
    Wei Huang
    Hong-Li Suo
    Wen Ma
    Rare Metals, 2019, 38 (07) : 689 - 694
  • [25] Preparation of La2Ce2O7 Powder by Citric Acid Method for Thermal Barrier Coatings
    Zhang Hongsong
    Liao Suran
    Du Hongli
    RARE METAL MATERIALS AND ENGINEERING, 2011, 40 : 481 - 484
  • [26] La2Ce2O7/YSZ热障涂层抗CMAS腐蚀及机制研究
    尹冰冰
    夏杰
    刘巍巍
    杨丽
    周益春
    湘潭大学学报(自然科学版), 2020, 42 (03) : 62 - 72
  • [27] Influence of Gd2O3 addition on thermophysical properties of La2Ce2O7 ceramics for thermal barrier coatings
    Zhang Hong-song
    Chen Xiao-ge
    Li Gang
    Wang Xin-li
    Dang Xu-dan
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2012, 32 (14) : 3693 - 3700
  • [28] Solid Particle Erosion Behavior of La2Ce2O7/YSZ Double-Ceramic-Layer and Traditional YSZ Thermal Barrier Coatings at High Temperature
    Zhao, Xianli
    Liu, Wei
    Li, Cong
    Yan, Gang
    Wang, Qianwen
    Yang, Li
    Zhou, Yichun
    COATINGS, 2022, 12 (11)
  • [29] Investigation about thermal conductivities of La2Ce2O7 doped with calcium or magnesium for thermal barrier coatings
    Zhang Hong-song
    Wei Yuan
    Li Gang
    Chen Xiao-ge
    Wang Xin-Li
    JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 537 : 141 - 146
  • [30] CMAS corrosion resistance of YSZ thermal barrier coatings with Al2O3 and YSZ-Al2O3 protective layers
    Ru, Pei-wen
    Hu, Yi
    Yang, Yong
    Zhao, Hong-jian
    Shao, Yu-xuan
    Wang, Yan-wei
    Li, Wei
    Wang, Xing-yu
    Sun, Wen-wei
    Ma, Yu-duo
    CERAMICS INTERNATIONAL, 2024, 50 (21) : 44401 - 44416
12345