Electrochemical behavior of graphite anode during anode effect in cryolite molten salts

Anodic electrochemical behavior was studied on graphite anode at 1000 degrees C in cryolite-alumina molten salt by means of cyclic voltammetry. The high current peak in a typical cyclic voltammogram was discussed. It is considered that a type of oxyfluoroaliminate complex anions reacts with carbon to form a high-resistance CF film on the anode surface at a high potential. The passivation potential is 3.28 V in 0.5% alumina-containing electrolyte, and the passivation potential increases with alumina content increasing which indicates that the alumina content determines the anodic process in the cryolite-alumina molten salt system.