Experimental Study on Intermittent Turning 2.25Cr-1Mo-0.25V Steel with Coated Cemented Carbide Tool

被引：2
|
作者：
Liu, Hanlian [1 ]
Lv, Xiang [1 ]
Huang, Chuanzhen [1 ]
Zhu, Hongtao [1 ]
机构：
[1] Shandong Univ, Sch Mech Engn, Minist Educ, Ctr Adv Jet Engn Technol CaJET,Key Lab High Effic, Jinan 250061, Peoples R China
来源：
ADVANCES IN MATERIALS PROCESSING X | 2012年 / 500卷
关键词：
Shell ring material; Intermittent turning; Efficient machining; Failure mechanism;
D O I：
10.4028/www.scientific.net/AMR.500.128
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
In order to improve the machining efficiency and tool life in manufacturing process of hydrogenation reactor shell components, the cutting performance of quadrate GC4235 coated carbide tool in intermittent turning 2.25Cr-1Mo-0.25V steel was investigated, the optimal cutting parameters were obtained. The empirical mathematical models of relationships among the amount of metal removal, tool life, cutting force and cutting parameters were established. The failure mechanism of the GC4235 carbide coated tools for turning 2.25Cr-1Mo-0.25V steel at lower speed intermittent turning was abrasive wear and the coating peeling; however coating peeling and substrate adhesive wear were the main failure forms at the higher speed.
引用
收藏
页码：128 / 133
页数：6
相关论文
共 50 条
  • [31] 2.25Cr-1Mo-0.25V钢焊缝扩散氢分布试验
    金卿
    王迎君
    刘应虎
    叶小松
    许凯
    压力容器, 2019, 36 (01) : 20 - 23
  • [32] 2.25Cr-1Mo-0.25V钢板热处理工艺试验
    薛巍
    李南
    党兆凯
    压力容器, 2004, (10) : 10 - 13
  • [33] EFFECTS OF TEMPERING TEMPERATURE ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF GRANULAR BAINITE IN 2.25Cr-1Mo-0.25V STEEL
    Jiang Zhonghua
    Wang Pei
    Li Dianzhong
    Li Yiyi
    ACTA METALLURGICA SINICA, 2015, 51 (08) : 925 - 934
  • [34] Rietveld quantitative analysis of carbides precipitation in normalized-tempered 2.25Cr-1Mo-0.25V steel
    Zhang Yongtao
    Zhao Sixin
    Liang Jiamiao
    Zhang Hanqian
    Li Jinfu
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2009, 24 (06): : 922 - 926
  • [35] Rietveld Quantitative Analysis of Carbides Precipitation in Normalized-tempered 2.25Cr-1Mo-0.25V Steel
    张永涛
    张汉谦
    Journal of Wuhan University of Technology(Materials Science), 2009, (06) : 922 - 926
  • [36] Rietveld quantitative analysis of carbides precipitation in normalized-tempered 2.25Cr-1Mo-0.25V steel
    Yongtao Zhang
    Sixin Zhao
    Jiamiao Liang
    Hanqian Zhang
    Jinfu Li
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2009, 24 : 922 - 926
  • [37] Thermal simulation experiments of welding heat affected zone of 2.25Cr-1Mo-0.25V heat resistance steel
    Key Laboratory of Metastable Materials Science and Technology, College of Materials Science and Engineering, Yanshan University, Qinhuangdao 066004, China
    不详
    Cailiao Rechuli Xuebao, 2007, 1 (66-70+74):
  • [38] Quantitative assessment of the hydrogen induced cracking for 2.25Cr-1Mo-0.25V steel under electrochemical charging conditions
    Wang, Y. F.
    Hu, S. Y.
    Tian, Z. Q.
    Cheng, G. X.
    ENGINEERING FAILURE ANALYSIS, 2021, 124
  • [39] Impact of Hot Bending on the High-Temperature Performance and Hydrogen Damage of 2.25Cr-1Mo-0.25V Steel
    Huang, Song
    Chen, Zhiping
    Li, You
    Zhang, Delin
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (01) : 567 - 577
  • [40] EVOLUTION OF SECOND PHASE IN 2.25Cr-1Mo-0.25V STEEL WELD METAL DURING HIGH TEMPERATURE TEMPERING
    Tao Peng
    Zhang Chi
    Yang Zhigang
    Hiroyuki, Takeda
    ACTA METALLURGICA SINICA, 2009, 45 (01) : 51 - 57
12345