Mechanism of improvement on strength and toughness of H13 die steel by nitrogen

The mechanism of nitrogen addition to AISI H13 die steel is proposed and supported using thermodynamic calculations in addition to observed changes in precipitate, microstructure, crystal structure, and macroproperties. The results indicate that the average impact toughness ak of the novel nitrogen H13 steel is maximally 17.6J cm(-2) and minimally 13.4J cm(-2). These values result in die steel that reaches premium grade and approximate the superior grade as specified in NADCA#207-2003, additionally the hardness is improved 3-5HRC. Experimental findings indicate that the residual V(C,N) particles undissolved during nitrogen H13 steel austenitizing by quenching helps to suppress growth of original austenitic crystal grains, this in turn results in finer martensitic structures after quenching. In the subsequent tempering process all N atoms are dissolved in the solid state matrix a result of C atoms displacing N atoms in V(C,N). Solid dissolution of N atoms produces a distorted lattice of Fe matrix which results in an increase in the hardness of the steel. Additionally this displacement reaction is important for slow growth of secondary particles in nitrogen H13 steel during the tempering process which helps to increase impact toughness compared to its nitrogen-free counterpart given the same condition of heat-treatment. (C) 2015 Elsevier B.V. All rights reserved.