In-Situ Observation on the Diversified Morphology and Growth Behavior of Al3Ni Phase at the Liquid Al/Solid Ni Interface

被引：9
|
作者：
Ding, Zongye [1 ]
Hu, Qiaodan [1 ]
Lu, Wenquan [1 ]
Sun, Siyu [1 ]
Xia, Mingxu [1 ]
Li, Jianguo [1 ]
机构：
[1] Shanghai Jiao Tong Univ, Sch Mat Sci & Engn, Shanghai Key Lab Mat Laser Proc & Modificat, Shanghai 200240, Peoples R China
来源：
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2018年 / 49A卷 / 05期
基金：
中国国家自然科学基金;
关键词：
MICROSTRUCTURAL EVOLUTION; SOLDERING REACTION; DIFFUSION COUPLES; DISSOLUTION; ALUMINUM; NICKEL; SOLIDIFICATION; KINETICS; ALLOY; AL/NI;
D O I：
10.1007/s11661-018-4537-z
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The morphology and growth behavior of Al3Ni in the liquid Al/solid Ni interface were observed through synchrotron radiation. The formation time and mechanism of Al3Ni are connected with saturation of the molten layer. In unsaturated conditions, the growth of columnar Al3Ni formed during solidification governed by the melting of small grains accompanied by the growth of adjacent large grains and coalescence of grains near the tips. Conversely, the scallop-type Al3Ni formed in holding showed annexation of adjacent small grains with its morphology changing from scallop to hemisphere.
引用
收藏
页码：1486 / 1491
页数：6
相关论文
共 50 条
  • [21] Effect of cooling rate on the 3D morphology of the proeutectic Al3Ni intermetallic compound formed at the Al/Ni interface after solidification
    Yu, Liao
    Hu, Qiaodan
    Ding, Zongye
    Yang, Fan
    Lu, Wenquan
    Zhang, Naifang
    Cao, Sheng
    Li, Jianguo
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2021, 69 : 60 - 68
  • [22] 3D morphology and growth mechanism of primary Al3Ni in directionally solidified Al-16 wt% Ni alloy
    Zhang, Naifang
    Lu, Wenquan
    Ding, Zongye
    Hu, Qiaodan
    Li, Jianguo
    JOURNAL OF ALLOYS AND COMPOUNDS, 2023, 938
  • [23] Effect of cooling rate on the 3D morphology of the proeutectic Al3Ni intermetallic compound formed at the Al/Ni interface after solidification
    Liao Yu
    Qiaodan Hu
    Zongye Ding
    Fan Yang
    Wenquan Lu
    Naifang Zhang
    Sheng Cao
    Jianguo Li
    JournalofMaterialsScience&Technology, 2021, 69 (10) : 60 - 68
  • [24] A New Sight of the Growth Characteristics of Solidified Al3Ni at the Liquid-Solid Interface by Synchrotron Radiography and 3D Tomography
    Ding, Zongye
    Hu, Qiaodan
    Yang, Fan
    Lu, Wenquan
    Yang, Tianxing
    Cao, Sheng
    Li, Jianguo
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2020, 51 (06): : 2689 - 2696
  • [25] The optical properties of Al3Ni
    Cubiotti, G
    Laine, AD
    Mondio, G
    Krasovskii, EE
    Krasovska, OV
    Kucherenko, YN
    Antonov, VN
    Kudryavtsev, YV
    Ivanchenko, VG
    JOURNAL OF PHYSICS-CONDENSED MATTER, 1996, 8 (15) : 2549 - 2555
  • [26] FRACTURE BEHAVIOR OF CRYSTALLINE AL3NI INTERMETALLIC FIBERS
    BROOM, ND
    DAVIES, GJ
    PHILOSOPHICAL MAGAZINE, 1973, 28 (03): : 685 - 702
  • [27] Growth temperature measurements and solidification microstructure selection of primary Al3Ni and eutectic in the αAl-Al3Ni system
    Juarez-Hernandez, A
    Jones, H
    SCRIPTA MATERIALIA, 1998, 38 (05) : 729 - 734
  • [28] A nanoindentation study on Al3Ni interface of Ni reinforced aluminum-silicon composite
    Miranda, G.
    Madeira, S.
    Silva, F. S.
    Carvalho, O.
    MECHANICS OF ADVANCED MATERIALS AND STRUCTURES, 2017, 24 (10) : 871 - 874
  • [29] Magnetically aligned Al3Ni phase in Al-Ni alloys solidified with a high magnetic field
    Wang, Hui
    Wang, Qiuliang
    Ren, Zhongming
    Yan, Luguang
    2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 1055 - +
  • [30] ELECTROLYTIC PREPARATION OF AL3NI FIBERS FROM THE EUTECTIC ALLOY, AL-AL3NI
    QUINLAN, KP
    HUTTA, JJ
    MATERIALS RESEARCH BULLETIN, 1980, 15 (06) : 707 - 714
12345