A sol-gel dip/spin coating method to prepare titanium oxide films

被引：38
|
作者：
Wang, Xiaodong [1 ]
Shi, Fang [1 ]
Gao, Xiaoxia [1 ]
Fan, Caimei [2 ]
Huang, Wei [1 ]
Feng, Xianshe [3 ]
机构：
[1] Taiyuan Univ Technol, Key Lab Coal Sci & Technol, Minist Educ & Shanxi Prov, Taiyuan 030024, Peoples R China
[2] Taiyuan Univ Technol, Coll Chem & Chem Engn, Taiyuan 030024, Peoples R China
[3] Univ Waterloo, Dept Chem Engn, Waterloo, ON N2L 3G1, Canada
来源：
THIN SOLID FILMS | 2013年 / 548卷
基金：
中国国家自然科学基金; 中国博士后科学基金;
关键词：
Spin-coating; Titania; Thin films; Photocatalysis; Sol-gel; MEMBRANES; PERFORMANCE; DEPOSITION; CATALYSIS; FLOW;
D O I：
10.1016/j.tsf.2013.08.056
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A dip/spin coating method for the preparation of titanium oxide films was proposed. Instead of placing an oxide sol on top of a substrate surface, the dip/spin coating was accomplished on the lower surface of the substrate where gravitational force exerted on the colloidal particles during spreading under a centrifugal force. The resulting TiO2 films were compared to those prepared using the conventional spin-coating and dip-coating methods. All the films were found to be composed primarily of anatase with a small amount of brookite. Compared to the films prepared using the conventional spin-coating and dip-coating methods, the TiO2 films fabricated using the dip/spin method had small and uniform grains with a unique structure, resulting in an increased photocatalytic activity when tested for degradation of methyl orange under UV irradiation. (C) 2013 Published by Elsevier B.V.
引用
收藏
页码：34 / 39
页数：6
相关论文
共 50 条
  • [41] Structural and optical properties of ZnO thin films by the spin coating Sol-Gel method
    E. F. Keskenler
    S. Doğan
    B. Diyarbakır
    S. Duman
    B. Gürbulak
    Journal of Sol-Gel Science and Technology, 2011, 60 : 66 - 70
  • [42] Full Investigation of Angle Dependence in Dip-Coating Sol-Gel Films
    Bottein, Thomas
    Loizillon, Jerome
    Grosso, David
    JOURNAL OF PHYSICAL CHEMISTRY B, 2017, 121 (25): : 6220 - 6225
  • [43] Structural and optical properties of ZnO thin films by the spin coating Sol-Gel method
    Keskenler, E. F.
    Dogan, S.
    Diyarbakir, B.
    Duman, S.
    Gurbulak, B.
    JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2011, 60 (01) : 66 - 70
  • [44] Coating of LaCoO3 thin film with sol-gel dip coating method
    Okuyucu, Hasan
    Dahl, Paul Inge
    Einarsrud, Mari Ann
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2008, 8 (02) : 685 - 688
  • [45] Preparation and characterization of ZnO thin films deposited by sol-gel spin coating method
    Department of Physics, Faculty of Science, Anadolu University, 26470 Eskisehir, Turkey
    J. Optoelectron. Adv. Mat., 2008, 10 (2578-2583):
  • [46] Preparation and characterization of ZnO thin films deposited by sol-gel spin coating method
    Ilican, S.
    Caglar, Y.
    Caglar, M.
    JOURNAL OF OPTOELECTRONICS AND ADVANCED MATERIALS, 2008, 10 (10): : 2578 - 2583
  • [47] Synthesis and characterization of nanocrystalline TiO2 thin films by sol-gel dip coating method
    Gokilamani, N.
    Muthukumarasamy, N.
    Thambidurai, M.
    ADVANCES IN NANOSCIENCE AND NANOTECHNOLOGY, 2013, 678 : 108 - +
  • [48] The microstructure of Al-doped ZnO thin films by a sol-gel dip-coating method
    Jun, Min-Chul
    Park, Sang-Uk
    Lee, Kyung-Ju
    Moon, Byung-Moo
    Koh, Jung-Hyuk
    JOURNAL OF CERAMIC PROCESSING RESEARCH, 2012, 13 (06): : 721 - 724
  • [49] Synthesis and Characterization of Thin TiO2 Films Using the Sol-gel dip Coating Method
    Woo-Garcia, R. M.
    Garcia-Gonzalez, L.
    Arguelles-Lucho, P.
    Guarneros-Aguilar, C.
    Cervantes, B.
    Herrera-May, A. L.
    Lopez-Huerta, F.
    2020 5TH INTERNATIONAL CONFERENCE ON ENERGY MATERIALS AND APPLICATIONS, 2020, 908
  • [50] Low-Temperature Synthesis of Vanadium Dioxide Thin Films by Sol-Gel Dip Coating Method
    Chotirat, Ladawan
    Niyomwas, Sutham
    Wongpisan, Witthawat
    Supothina, Sitthisuntorn
    JOURNAL OF NANOTECHNOLOGY, 2021, 2021
12345