Oxidation behavior of the directionally solidified Ni-base superalloy DS951 in air

被引：15
|
作者：
Huang, L [1 ]
Sun, XF [1 ]
Guan, HR [1 ]
Hu, ZQ [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Superalloy Dept, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
来源：
OXIDATION OF METALS | 2005年 / 64卷 / 5-6期
关键词：
Ni-base superalloy; DS951; oxidation; kinetics; microstructure;
D O I：
10.1007/s11085-005-8529-1
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The isothermal oxidation behavior at 1000, 1050 and 1100 degrees C and the cyclic oxidation behavior at 1000 degrees C of the directionally solidified Ni-base superalloy DS951 were investigated. The oxidized samples were characterized by SEM, EDAX, XRD. The alloy DS951 obeyed a two-stage parabolic rate law during isothermal oxidation at 1000-1100 degrees C. In cyclic conditions, the alloy showed no weight loss even after 1100 cycles. Cross-sectional examination revealed the development of faceted and needle-shaped AlN precipitates in the alloy subsurface region during cyclic oxidation, while no internal corrosion products were found in isothermal tests. Furthermore, a selective oxidation of MC carbides (M was predominately niobium with some chromium and tungsten) was observed along alloy grain boundaries and in interdendritic areas.
引用
收藏
页码：303 / 318
页数：16
相关论文
共 50 条
  • [21] Microstructural evolution in directionally solidified Ni-base superalloy IN792+Hf
    Seo, S. M.
    Kim, I. S.
    Lee, J. H.
    Jo, C. Y.
    Miyahara, H.
    Ogi, K.
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2008, 24 (01) : 110 - 114
  • [22] PLASTIC DEFORMATION AND DISLOCATION STRUCTURE IN γ'-PHASE OF A DIRECTIONALLY SOLIDIFIED Ni-BASE SUPERALLOY
    WEN Mao LIN Dongliang T.L.Lin Shanghai Jiaotong University
    Acta Metallurgica Sinica(English Letters), 1990, (02) : 79 - 88
  • [23] Microstructural Evolution in Directionally Solidified Ni-Base Superalloy IN792+Hf
    S.M.Seo
    I.S.Kim
    J.H.Lee
    C.Y.Jo
    H.Miyahara
    K.Ogi
    Journal of Materials Science & Technology, 2008, (01) : 110 - 114
  • [24] Parameters influencing thermomechanical fatigue of a directionally-solidified Ni-base superalloy
    Kirka, M. M.
    Brindley, K. A.
    Neu, R. W.
    Antolovich, S. D.
    Shinde, S. R.
    Gravett, P. W.
    INTERNATIONAL JOURNAL OF FATIGUE, 2015, 81 : 48 - 60
  • [25] Thermomechanical fatigue experimental study on a notched directionally solidified Ni-base superalloy
    Hu, Xiaoan
    Shi, Duoqi
    Yang, Xiaoguang
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 674 : 451 - 458
  • [26] Microstructural evolution in directionally solidified Ni-base superalloy IN792+Hf
    Seo, S.M.
    Kim, I.S.
    Lee, J.H.
    Jo, C.Y.
    Miyahara, H.
    Ogi, K.
    Journal of Materials Science and Technology, 2008, 24 (01): : 110 - 114
  • [27] Tensile and fracture behavior of DZ951 Ni-base superalloy
    储昭贶
    于金江
    孙晓峰
    赵乃仁
    管恒荣
    胡壮麒
    Transactions of Nonferrous Metals Society of China, 2006, (S3) : 1949 - 1952
  • [28] Tensile and fracture behavior of DZ951 Ni-base superalloy
    Chu Zhao-kuang
    Yu Jin-jiang
    Sun Xiao-feng
    Zhao Nai-ren
    Guan Heng-rong
    Hu Zhuang-qi
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2006, 16 : S1949 - S1952
  • [29] Very High Cycle Fatigue Behavior of a Directionally Solidified Ni-Base Superalloy DZ4
    Nie, Baohua
    Zhao, Zihua
    Liu, Shu
    Chen, Dongchu
    Ouyang, Yongzhong
    Hu, Zhudong
    Fan, Touwen
    Sun, Haibo
    MATERIALS, 2018, 11 (01):
  • [30] THERMOMECHANICAL FATIGUE OF A DIRECTIONALLY-SOLIDIFIED NI-BASE SUPERALLOY IN THE PRESENCE OF STRESS CONCENTRATIONS
    Kupkovits, Robert A.
    Neu, Richard W.
    PROCEEDINGS OF THE ASME TURBO EXPO 2009, VOL 6, PTS A AND B, 2009, : 163 - 173
12345