Mechanical Behaviour of Advanced Composite Laminates Embedded with Carbon Nanotubes - Review

Embedding carbon nanotubes (CNTs) in load-bearing composite laminate hosts and thereby turning them into nano-laminates is a rapidly emerging field and has tremendous potential in enhancing mechanical performance of host laminates. This state-of-the-art review intends to provide physical insight into the understanding of enhancing mechanisms of processed and controlled CNTs in nano-laminates. It focuses on four aspects: (1) physical characteristics of CNTs including CNT length, diameter and weight percentage; (2) processing and control techniques of CNTs in fabrication of nano-laminates including distribution, dispersion and orientation controls of CNTs; (3) mechanical properties along with their testing methods including tension, in-plane compression, interlaminar shear (ILS), flexure, mode I and mode II fracture toughness as well as compression-after-impact (CAI); and (4) post-mortem microscopic corroborative evidence after mechanical testing. As this review indicates, selective and uniform production of CNTs with specific dimensions and physical properties has yet to be achieved on a consistent basis. There is little control over CNT orientations in most fabrication processes of nano-laminates except for some cases associated with chemical vapour deposition (CVD). There are only two reports on the in-plane compression and there is none on in-plane shear. For reinforcement-dominated mechanical properties such as tension and flexure, there is little enhancement as reported. However, substantial enhancement in in-plane compression strength was reported. For matrix-dominated mechanical properties such as ILS strength and mode-I and mode-II fracture toughness, significant enhancement, albeit with substantially varying degrees, has been reported. In the meanwhile, the lack of consistent characterisation in those properties was also noticeable. Post-mortem microscopic corroborative evidence was very limited.