High temperature oxidation of Cr-Mo-V tool steel in carbon dioxide

被引：7

作者：

Chaliampalias, D. ^{[1
]}

Vourlias, G. ^{[1
]}

Pavlidou, E. ^{[1
]}

Chrissafis, K. ^{[1
]}

机构：

[1] Aristotle Univ Thessaloniki, GR-54006 Thessaloniki, Greece

来源：

JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY | 2013年 / 113卷 / 03期

关键词：

Metals and Alloys; Microstructure; Scanning Electron Microscopy; Thermogravimetric measurements; ALLOYS; METAL;

D O I：

10.1007/s10973-013-2947-0

中图分类号：

O414.1 [热力学];

学科分类号：

摘要：

This study aims to examine the oxidation resistance and kinetics of Cr, Mo, and V containing tool steel (Calmax) when exposed in CO2 high temperature environment by thermogravimetric measurements, X-ray diffraction analysis, and microscopic observation. The tool steel samples begin to oxidize at 480 A degrees C while over 600 A degrees C, the oxidation rate increases significantly. Finally, at 900 A degrees C, the oxidation rate is significantly high. The activation energy of the oxidation was calculated as 160.1 kJ mol(-1). Microscopically, the thickness of the scale was found to increase with the exposure temperature, and the as formed scales consisted of two distinguishable oxide layers.

引用

页码：1309 / 1315

页数：7

共 50 条

[1] High temperature oxidation of Cr–Mo–V tool steel in carbon dioxide
D. Chaliampalias
G. Vourlias
E. Pavlidou
K. Chrissafis
Journal of Thermal Analysis and Calorimetry, 2013, 113 : 1309 - 1315
[2] Examination of the oxidation resistance of Cr-Mo-V tool steel by thermal analysis
Chaliampalias, D.
Vourlias, G.
Pavlidou, E.
Chrissafis, K.
JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 2012, 108 (02) : 677 - 684
[3] HIGH-TEMPERATURE CREEP DEFORMATION OF A CR-MO-V STEEL
KIMURA, K
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (05): : S487 - S487
[4] Hydrogen effect on high-temperature degradation of a Cr-Mo-V steel
Nykyforchyn, HM
Schaper, M
Student, OZ
Loniuk, BP
ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III, 1996, : 1527 - 1532
[5] Improvement of high-temperature Cr-Mo-V steel for power equipment
Kulikova L.V.
Shevakin A.F.
Pantyukhin A.P.
Steel in Translation, 2014, 44 (11) : 854 - 856
[6] Microstructure and high temperature wear resistance of Cr-Mo-V cast hot-forging tool steel
School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, China
不详
Tezhong Zhuzao Ji Youse Hejin, 2007, 6 (459-461): : 459 - 461
[7] Effect of Temperature on Oxidation Behavior of Cr-Mo-V Steel with Different Cr Contents for High-Speed Train Brake Discs
Wu, Dan
Wang, Fuming
Li, Changrong
Zheng, Yaxu
Shen, Wei
9TH INTERNATIONAL SYMPOSIUM ON HIGH-TEMPERATURE METALLURGICAL PROCESSING, 2018, : 503 - 512
[8] TEMPER BRITTLENESS OF CR-MO-V STEEL
MOROZOV, AM
NIKOLAEV, VA
PARSHIN, AM
RYBIN, VV
METAL SCIENCE AND HEAT TREATMENT, 1977, 19 (5-6) : 461 - 465
[9] Influence of melt undercooling on the microstructure of levitated Cr-Mo-V tool steel
Grgac, P.
Liptak, M.
Behulova, M.
Caplovic, L.
Lindenkreuz, H. -G
Loeser, W.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 449 : 658 - 661
[10] Fatigue fracture behavior of high strength Cr-Mo-V steel
National Key Lab. of Advanced Steel Processing Technology and Materials, Beijing 100081, China
不详
不详
不详
Cailiao Rechuli Xuebao, 2007, 5 (37-41):

← 1 2 3 4 5 →