Corrosion Behavior of AZ61 Magnesium Alloys in NaCl Solution

被引：1
|
作者：
Chai Yue-sheng [1 ,2 ]
Wang Li-na [2 ]
Sun Gang [1 ,2 ]
Sun Shu-li [2 ]
Zhang Min-gang [1 ,2 ]
机构：
[1] Shanxi Prov Engn & Technol Res Ctr Mg & Mg Alloy, Taiyuan 030024, Shanxi, Peoples R China
[2] Taiyuan Univ Sci & Technol, Coll Mat Sci & Engn, Taiyuan, Shanxi 030024, Peoples R China
来源：
ADVANCED MATERIALS, PTS 1-4 | 2011年 / 239-242卷
关键词：
corrosion rate; Cl- ion concentration; corrosion time; magnesium alloy;
D O I：
10.4028/www.scientific.net/AMR.239-242.2240
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
Magnesium alloys are used widely because of its good performance. However, its practical application is restricted by low corrosion resistance. In this study, the effects of corrosion time and NaCl concentration on the corrosion behavior of AZ61 magnesium alloy were investigated from the corrosion morphology and the corrosion rate. These results have displayed that the corrosion rate of AZ61 magnesium alloy decreases with the increasing etching time. Meanwhile, the corrosion rate of AZ61 magnesium alloy increases with the increasing sodium chloride concentration. This is mainly because that the Cl- ion in the solution destroys the protective film on the surface of magnesium alloy and the high Cl- ion concentration accelerates the corrosion rate.
引用
收藏
页码：2240 / +
页数：2
相关论文
共 50 条
  • [41] Effect of CaO and Hot Extrusion on the Oxidation of AZ61 Magnesium Alloys
    Lee, Dong Bok
    OXIDATION OF METALS, 2016, 85 (1-2): : 65 - 74
  • [42] Tensile and fatigue behaviour of wrought magnesium alloys AZ31 and AZ61
    Chamos, A. N.
    Pantelakis, Sp. G.
    Haidemenopoulos, G. N.
    Kamoutsi, E.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2008, 31 (09) : 812 - 821
  • [43] Hot deformation behavior and dynamic recrystallization kinetics of AZ61 and AZ61
    Sani, S. Aliakbari
    Ebrahimi, G. R.
    Rashid, A. R. Kiani
    JOURNAL OF MAGNESIUM AND ALLOYS, 2016, 4 (02) : 104 - 114
  • [44] Formation and properties of stannate conversion coatings on AZ61 magnesium alloys
    Lin, CS
    Lin, HC
    Lin, KM
    Lai, WC
    CORROSION SCIENCE, 2006, 48 (01) : 93 - 109
  • [45] Effect of CaO and Hot Extrusion on the Oxidation of AZ61 Magnesium Alloys
    Dong Bok Lee
    Oxidation of Metals, 2016, 85 : 65 - 74
  • [46] Effect of hydrogen on fatigue crack propagation behavior of wrought magnesium alloy AZ61 in NaCl solution under controlled cathodic potentials
    Kakiuchi, Toshifumi
    Uematsu, Yoshihiko
    Hatano, Yuji
    Nakajima, Masaki
    Nakamura, Yuki
    Taniguchi, Tomonori
    ENGINEERING FRACTURE MECHANICS, 2015, 137 : 88 - 96
  • [47] High-temperature mechanical properties of AZ61 and AZ61-0.7Si magnesium alloys
    Geranmayeh, R.
    Mahmudi, R.
    Movahedi-Rad, A.
    Malekoshoaraei, M. H.
    KOVOVE MATERIALY-METALLIC MATERIALS, 2012, 50 (06): : 393 - 397
  • [48] Corrosion fatigue behavior of extruded magnesium alloy AZ61 under three different corrosive environments
    Bhuiyan, Md. Shahnewaz
    Mutoh, Yoshiharu
    Murai, Tsutomu
    Iwakami, Shinpei
    INTERNATIONAL JOURNAL OF FATIGUE, 2008, 30 (10-11) : 1756 - 1765
  • [49] Stress Corrosion Cracking Behavior of Fine-Grained AZ61 Magnesium Alloys Processed by Equal-Channel Angular Pressing
    Xie, Qiuyuan
    Ma, Aibin
    Jiang, Jinghua
    Cheng, Zhaojun
    Song, Dan
    Yuan, Yuchun
    Liu, Huan
    METALS, 2017, 7 (09)
  • [50] Anomalous hydrogen evolution on AZ31, AZ61 and AZ91 magnesium alloys in unbuffered sodium chloride solution
    Fajardo, S.
    Bosch, J.
    Frankel, G. S.
    CORROSION SCIENCE, 2019, 146 : 163 - 171
12345