Study of corrosive fatigue and life enhancement of low pressure steam turbine blade using friction dampers

被引：10

作者：

Bhagi, Loveleen Kumar ^{[1
]}

Rastogi, Vikas ^{[2
]}

Gupta, Pardeep ^{[1
]}

机构：

[1] St Longowal Inst Engn & Technol, Dept Mech Engn, Longowal 148106, Punjab, India

[2] Delhi Technol Univ, Dept Mech Prod Ind & Automobile Engn, Delhi 10042, India

来源：

JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY | 2017年 / 31卷 / 01期

关键词：

Steam turbine blade; Fracture; Corrosion; Fatigue; Friction damper; Bondgraph modeling; FAILURE;

D O I：

10.1007/s12206-016-1203-5

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The paper investigates the causes of failure of low pressure steam turbine blade of the last stage and suggests few techniques to overcome the failure causes is presented in this paper. The blade under investigation is made of chrome alloy steel. The fracture occurred at the airfoil region of the blade. The investigation included visual inspection, micro structural characterization, SEM-EDS microanalysis and spectroscopy test to identify the causes of failure. The paper also suggests the methods to reduce the blade fatigue subsequently through computation and to enhance the fatigue strength of the steam turbine blade. In order to reduce the blade fatigue susceptibility and to enhance the fatigue life of the steam turbine blade, the wedge shape friction damper is proposed.

引用

页码：17 / 27

页数：11

共 50 条

[41] TURBINE BLADE CRACK DETECTION USING BLADE VIBRATION MONITORING: FIELD STUDY FROM AN OPERATING STEAM TURBINE
Techy, Laszlo
De Gooyer, Brynn
von Flotow, Andy
Tappert, Peter
John, Shaju
Losh, David
Lewit, Benjamin
PROCEEDINGS OF ASME TURBO EXPO 2022: TURBOMACHINERY TECHNICAL CONFERENCE AND EXPOSITION, GT2022, VOL 8A, 2022,
[42] Study for Fracture in the Last Stage Blade of a Low Pressure Turbine
Lee, Gil Jae
Kim, Jae Hoon
TRANSACTIONS OF THE KOREAN SOCIETY OF MECHANICAL ENGINEERS A, 2016, 40 (04) : 423 - 428
[43] Implications of day temperature for a high-pressure-turbine blade's low-cycle-fatigue life consumption
Naeem, Muhammad
JOURNAL OF PROPULSION AND POWER, 2008, 24 (03) : 624 - 628
[44] EFFECT OF STEAM INJECTION ON LAST-STAGE BLADE TEMPERATURE OF LOW PRESSURE STEAM TURBINE AT LOW VOLUME FLOW CONDITION
Ma, Can
Wu, Jun
Lin, Yuansheng
PROCEEDINGS OF THE 25TH INTERNATIONAL CONFERENCE ON NUCLEAR ENGINEERING, 2017, VOL 6, 2017,
[45] Experimental Study on Dry Friction Damping Characteristics of the Steam Turbine Blade Material with Nonconforming Contacts
Wu, Jun
Yuan, Ruishan
He, Zhenwu
Zhang, Di
Xie, Yonghui
ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2015, 2015
[46] The influence of corrosion pits on the fatigue life of 17-4PH steam turbine blade steel
Schoenbauer, Bernd M.
Stanzl-Tschegg, Stefanie E.
Perlega, Andrea
Salzman, Ronald N.
Rieger, Neville F.
Turnbull, Alan
Zhou, Shengqi
Lukaszewicz, Mikolaj
Gandy, David
ENGINEERING FRACTURE MECHANICS, 2015, 147 : 158 - 175
[47] Experimental evaluation of high temperature low cycle fatigue/creep life of turbine blade
Wang, Yan-Rong
Song, Zhao-Hong
Hou, Gui-Cang
Hangkong Dongli Xuebao/Journal of Aerospace Power, 2002, 17 (04): : 407 - 411
[48] Localized Damage Identification in the Last Stage Low-Pressure Steam Turbine Blade Using Dynamic Parameter Measurements
Shetkar, Keshav Ramesh
Srinivas, J.
JOURNAL OF NONDESTRUCTIVE EVALUATION, DIAGNOSTICS AND PROGNOSTICS OF ENGINEERING SYSTEMS, 2023, 6 (01):
[49] Crack evaluation and subsequent solution of the last stage blade in a low-pressure steam turbine
Kim, Hyojin
Kang, Yongho
ENGINEERING FAILURE ANALYSIS, 2010, 17 (06) : 1397 - 1403
[50] Sensors and Methods for Blade Damage Operational Assessment in Low-Pressure Steam Turbine Stages
Prochazka, Pavel
Vanek, Frantisek
DAMAGE ASSESSMENT OF STRUCTURES X, PTS 1 AND 2, 2013, 569-570 : 726 - +

← 1 2 3 4 5 →