The effect of surface defects on the wear of Nylon 66 under dry and water lubricated sliding

被引：17
|
作者：
Abdelbary, A. [1 ]
Abouelwafa, M. N. [1 ]
El Fahham, I. M. [1 ]
Hamdy, A. H. [1 ]
机构：
[1] Univ Alexandria, Dept Mech Engn, Fac Engn, Alexandria, Egypt
来源：
TRIBOLOGY INTERNATIONAL | 2013年 / 59卷
关键词：
Wear; Nylon; 66; Surface crack; Cyclic load; MECHANISMS; POLYAMIDE-66;
D O I：
10.1016/j.triboint.2012.06.004
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
In polymeric bearing applications it was found that the polymer tends to wear more quickly than indicated in laboratory wear tests. The reason has been attributed to the effect of loading conditions and the generation of fatigue surface cracks. The current study investigated the effect of single imposed vertical crack in the Nylon 66 surface upon its wear behaviour in dry and water lubricated sliding conditions. The polymer was tested under different static and cyclic loading parameters. There was consistent evidence of the effect of surface crack on the wear rate under static and cyclic loading conditions. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：163 / 169
页数：7
相关论文
共 50 条
  • [41] The effect of oil pockets size and distribution on wear in lubricated sliding
    Koszela, Waldemar
    Pawlus, Pawel
    Galda, Lidia
    [J]. WEAR, 2007, 263 : 1585 - 1592
  • [42] Study on the surface microstructure evolution and wear property of bainitic rail steel under dry sliding wear
    Chen, Yuda
    Ren, Ruiming
    Zhao, Xiujuan
    Chen, Chunhuan
    Pan, Rui
    [J]. WEAR, 2020, 448
  • [43] The interaction of wear rate and friction with surface roughness for a lubricated sliding contact
    Barrell, DJW
    Priest, M
    [J]. Transient Processes in Tribology, 2004, 43 : 807 - 814
  • [44] The Effect of Load on Friction and Wear Behavior of NBR and FPM under Dry Sliding
    Lv, Xiaoren
    Sun, Hao
    Luo, Xuan
    Wang, Shijie
    [J]. ADVANCED MATERIALS, PTS 1-4, 2011, 239-242 : 985 - 989
  • [45] Comparative investigation of the tribological behavior and wear mechanism of bronze-graphite composite under dry-and water-lubricated sliding against steel
    Jia, Jun-Hong
    Zhou, Hui-Di
    Wang, Jing-Bo
    Zhou, Hua
    Chen, Jian-Min
    [J]. Mocaxue Xuebao/Tribology, 2002, 22 (01): : 36 - 39
  • [46] Wear behavior of SiC particulate reinforced aluminum composites sliding against steel balls under dry and lubricated conditions
    K.N. Tandon
    Z.C. Feng
    X.Y. Li
    [J]. Tribology Letters, 1999, 6 : 113 - 122
  • [47] THE WATER LUBRICATED, SLIDING WEAR BEHAVIOR OF POLYMERIC MATERIALS AGAINST STEEL
    CLARKE, CG
    ALLEN, C
    [J]. TRIBOLOGY INTERNATIONAL, 1991, 24 (02) : 109 - 118
  • [48] UHMWPE Hybrid Nanocomposites for Improved Tribological Performance Under Dry and Water-Lubricated Sliding Conditions
    Bin Ali, Annas
    Samad, M. Abdul
    Merah, N.
    [J]. TRIBOLOGY LETTERS, 2017, 65 (03)
  • [49] Wear behavior of SiC particulate reinforced aluminum composites sliding against steel balls under dry and lubricated conditions
    Tandon, KN
    Feng, ZC
    Li, XY
    [J]. TRIBOLOGY LETTERS, 1999, 6 (02) : 113 - 122
  • [50] OBSERVATIONS OF SURFACE TOPOGRAPHIES OF STEEL UNDER LUBRICATED WEAR
    ENDO, K
    IWAI, Y
    KONISHI, K
    [J]. JOURNAL OF JAPAN SOCIETY OF LUBRICATION ENGINEERS, 1977, 22 (12): : 796 - 802
12345