Hydrothermal synthesis and characterization of two novel three-dimensional vanadium phosphites: |(C10H10N2)| [V2IVO2(HPO3)2(H2PO3)2] and |(C4H16N3)| [V2IVVIIIO2F2(HPO3)4

被引：17
|
作者：
Jing, Xuemin [1 ]
Zhang, Lirong [1 ]
Gong, Shuzhe [1 ,2 ]
Li, Guanghua [1 ]
Bi, Minghui [1 ]
Huo, Qisheng [1 ]
Liu, Yunling [1 ]
机构：
[1] Jilin Univ, Coll Chem, State Key Lab Inorgan Synth & Preparat Chem, Changchun 130012, Peoples R China
[2] Daqing Normal Univ, Dept Chem, Daqing 163712, Peoples R China
来源：
MICROPOROUS AND MESOPOROUS MATERIALS | 2008年 / 116卷 / 1-3期
关键词：
Hydrothermal synthesis; Vanadium phosphites; Three-dimensional; Mixed valence;
D O I：
10.1016/j.micromeso.2008.03.026
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
Two novel three-dimensional vanadium phosphites vertical bar(C10H10N2)vertical bar [(V2VO2)-V-IV(HPO3)(2)(H2PO3)(2)] 1 and vertical bar(C4H16N3)vertical bar [(V2VO2F2)-V-IV-O-III(HPO3)(4)] 2 have been synthesized hydrothermally in the presence of structure-directing agents. Single-crystal structural analysis reveals that compound 1 has a three-dimensional open-framework with two different types of intersecting channels (monoclinic, P2(1)/n, a = 6.3541(14) angstrom, b = 10.460(2) angstrom, c = 14.769(3) angstrom, beta = 90.412(5)degrees, V = 981.6(4) angstrom(3), Z = 2 with R-1 = 0.0523), while compound 2 (orthorhombic, Pbca, a = 13.612(3) angstrom, b = 9.5753(19) angstrom, c = 14.022(3) angstrom, V = 1827.6(6) angstrom(3), Z = 4 with R-1 = 0.0441) presents a three-dimensional open-framework that consists of a novel {V3O14F2} trimer with mixed valence (V2VIII)-V-Iv linked by two bridging F atoms. In addition, it is worth noting that the organic templates plates play important roles in the formation of both novel structures. Further characterization of the two compounds has been performed, including X-ray powder diffraction, ICP, CHN, IR and TG-DTA analyses. (C) 2008 Elsevier Inc. All rights reserved.
引用
收藏
页码：101 / 107
页数：7
相关论文
共 50 条
  • [1] Synthesis and characterization of organically templated zinc phosphites with two- and three-dimensional structures, (C2N2H10)Zn2(HPO3)3 and(C4N2H12)Zn3(HPO3)4
    Lin, ZE
    Zhang, J
    Zheng, ST
    Yang, GY
    [J]. SOLID STATE SCIENCES, 2004, 6 (04) : 371 - 376
  • [2] Hydrothermal synthesis and structure characterization of C4H8N2H4•Zn(HPO3)2
    Shi, SH
    Li, GH
    Xin, HM
    Ding, H
    Xu, JN
    Zhu, GS
    Song, TY
    Qiu, SL
    [J]. CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE, 2004, 25 (02): : 230 - 232
  • [3] Hydrothermal syntheses, characterizations of novel three-dimensional indium phosphite and indium phosphite-phosphate with intersecting 8-membered ring channels: [In3(H2PO3)3(HPO3)4]•(trans-C6N2H16) and [In6(HPO3)8(H2PO3)5(H2PO4)]•(C3N2H12)2
    Huang, Liangliang
    Song, Tianyou
    Fan, Yong
    Yang, Lei
    Wang, Liping
    Zhang, Hua
    Wang, Li
    Xu, Jianing
    [J]. MICROPOROUS AND MESOPOROUS MATERIALS, 2010, 132 (03) : 409 - 413
  • [4] [Zn2(HPO3)2(H2PO3)][C3H5N2] and [Zn2(HPO3)3][C4H7N2]2•2H2O:: Two new layered zinc phosphites with double 12-membered rings templated by imidazole and 2-methylimidazole
    Liu, Li
    Liu, Yunling
    Li, Guanghua
    Chen, Chao
    Bi, Minghui
    Pang, Wenqin
    [J]. JOURNAL OF SOLID STATE CHEMISTRY, 2006, 179 (05) : 1312 - 1317
  • [5] Syntheses and structures of two chiral zincophosphite compounds:: [Zn(C8H8N2)(HPO3)] and (C6H13N2)[Zn3(C6H12N2)(HPO3)3(H2PO3)]
    Liu, Li
    Zhang, Li-rong
    Wang, Xiao-feng
    Li, Guang-hua
    Liu, Yun-ling
    Pang, Wen-qin
    [J]. DALTON TRANSACTIONS, 2008, 15 (15) : 2009 - 2014
  • [6] Synthesis, structure and magnetic characterization of a vanadium(IV) phosphite, [C2N2H10]• [(VO)3(H2O)(HPO3)4]•H2O
    Zhang, D
    Yue, HJ
    Shi, Z
    Guo, M
    Feng, SH
    [J]. MICROPOROUS AND MESOPOROUS MATERIALS, 2005, 82 (1-2) : 209 - 213
  • [7] Hydrothermal synthesis and structural characterization of two organically templated zincophosphites with three-dimensional frameworks, (C6H14N2)•[Zn3(HPO3)4] and (C4H12N2)•[Zn3(HPO3)4]
    Wang, L
    Shi, Z
    Fu, WS
    Li, GH
    Zhang, D
    Dong, WJ
    Dai, ZM
    Chen, XB
    Feng, SH
    [J]. JOURNAL OF SOLID STATE CHEMISTRY, 2004, 177 (01) : 80 - 88
  • [8] Hydrothermal synthesis and characterization of layered vanadium phosphite:: [HN(C2H4)3N][(VO)2(HPO3)2(OH)(H2O)]•H2O
    Shi, Z
    Zhang, D
    Li, GH
    Wang, L
    Lu, XY
    Hua, J
    Feng, SH
    [J]. JOURNAL OF SOLID STATE CHEMISTRY, 2003, 172 (02) : 464 - 470
  • [9] Hydrothermal synthesis and characterization of a vanadium(IV) phosphate phosphite with two-dimensional layered structures:: [V2O2(OH)(HPO3)(HPO3)0.7(PO3OH)0.3] • (C6N2H16)0.5
    Fu, WS
    Li, GH
    Wang, L
    Liang, GM
    Sun, YY
    Feng, SH
    [J]. CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE, 2005, 26 (09): : 1607 - 1609
  • [10] HYDROTHERMAL SYNTHESIS AND CHARACTERIZATION OF 2- AND 3-DIMENSIONAL SOLIDS OF THE OXOVANADIUM(IV)-PHOSPHITE SYSTEM - THE STRUCTURES OF [HN(ME)(CH2CH2)(2)N(ME)H]-[(VO)(4)(OH)(2)(HPO3)(4)], [H2N(CH2CH2)(2)NH2][(VO)(3)(HPO3)(4)(H2O)(2)], AND [VO(HPO3)(H2O)]
    BONAVIA, G
    DEBORD, J
    HAUSHALTER, RC
    ROSE, D
    ZUBIETA, J
    [J]. CHEMISTRY OF MATERIALS, 1995, 7 (11) : 1995 - &
12345