Permeation behavior of deuterium implanted into Ti-6A1-4V alloy

被引：0
|
作者：
Arita, M [1 ]
Hayashi, T [1 ]
Okuno, K [1 ]
Hayashi, Y [1 ]
机构：
[1] KYUSHU UNIV,FAC ENGN,DEPT MAT SCI & ENGN,HAKOZAKI,FUKUOKA 812,JAPAN
来源：
JOURNAL OF NUCLEAR MATERIALS | 1997年 / 248卷
关键词：
D O I：
10.1016/S0022-3115(97)00116-5
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Permeation of deuterium implanted into Ti-6Al-4V alloy has been studied using 0.5 keV D+ ion beam in the temperature range of 323 to 753 K. Above 600 K, the ratio of steady state permeation flux/incident flux ranges from 3.3 x 10(-3) at 633 K to 4.8 x 10(-3) at 753 K. The activation energy of permeation is about 0.12 eV in this temperature range. At temperatures below 600 K, the permeation flux of deuterium decreases drastically. Deuterium implanted in the lower temperature range desorbed from the alloy by heating after implantation. Thus, the most of the implanted ions remain in the alloy at low temperatures. (C) 1997 Elsevier Science B.V.
引用
收藏
页码：60 / 63
页数：4
相关论文
共 50 条
  • [21] Diffusion thermodynamic behavior of milling Ti-6A1-4V alloy in liquid nitrogen cryogenic cooling
    Wang, Fengbiao
    Hou, Bo
    Wang, Yongqing
    Liu, Haibo
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2018, 95 (5-8): : 2783 - 2793
  • [22] THE EFFECT OF ION PLATING ON THE FRICTION AND WEAR OF TI-6A1-4V ALLOY
    EYLON, D
    BETTS, RK
    FUJISHIRO, S
    THIN SOLID FILMS, 1980, 73 (02) : 323 - 329
  • [23] Hydrogen-induced hot workability in Ti-6A1-4V alloy
    宗影影
    单德彬
    吕炎
    郭斌
    TransactionsofNonferrousMetalsSocietyofChina, 2006, (S3) : 2072 - 2076
  • [24] SURFACE MODIFICATION OF TI-6A1-4V ALLOY BY SALT CYANIDING AND NITRIDING
    LAI, FD
    WU, TI
    WU, JK
    SURFACE & COATINGS TECHNOLOGY, 1993, 58 (01): : 79 - 81
  • [25] OXIDE ADHERENCE AND PORCELAIN BONDING TO TITANIUM AND TI-6A1-4V ALLOY
    ADACHI, M
    MACKERT, JR
    PARRY, EE
    FAIRHURST, CW
    JOURNAL OF DENTAL RESEARCH, 1990, 69 (06) : 1230 - 1235
  • [26] IMPROVEMENT IN FATIGUE LIFETIME OF TI-6A1-4V ALLOY BY BORON IMPLANTATION
    ZHANG, DW
    ZHANG, XP
    YU, WC
    WANG, ZG
    SURFACE & COATINGS TECHNOLOGY, 1993, 58 (02): : 119 - 123
  • [27] Diffusion thermodynamic behavior of milling Ti-6A1-4V alloy in liquid nitrogen cryogenic cooling
    Wang, Fengbiao (wangfb79@163.com), 1600, Springer London (95): : 5 - 8
  • [28] INITIATION OF STRESS-CORROSION CRACKING IN TI-6A1-4V ALLOY
    LINK, F
    MUNZ, D
    CORROSION SCIENCE, 1973, 13 (10) : 809 - &
  • [29] On diffusion bonding of Ti-6A1-4V
    Ravishankar, B
    Ramakrishnan, SS
    Angelo, PC
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2002, 55 (03): : 105 - 114
  • [30] METALLURGICAL OPTIMIZATION OF A COMMERCIAL-PURITY TI-6A1-4V ALLOY
    YODER, GR
    COOLEY, LA
    CROOKER, TW
    REPORT OF NRL PROGRESS, 1975, (DEC): : 16 - 19
12345