Features of Fracture and Fatigue Durability of the Maintained Steel of Disks of the Steam Turbine of Thermal Power Station

被引：0
|
作者：
Tkachuk, Yu. M. [1 ]
Student, O. Z.
机构：
[1] Lutsk Natl Tech Univ, UA-43018 Lutsk, Ukraine
来源：
METALLOFIZIKA I NOVEISHIE TEKHNOLOGII | 2011年 / 33卷
关键词：
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
As shown, the regulated values of mechanical properties under tension of the 34XH3M steel after operation during at congruent to 3.10(5) h as a disk of steam turbine is not satisfied that indicates on the steel degradation. As revealed, using fractography analysis, the nucleation of crack in the damaged disk of steam turbine appears by the mechanism of fretting fatigue due to low-amplitude displacements of blade roots into the disk groove, and its subsequent extension takes place by the mechanism of corrosion-fatigue crack growth. The characteristics of the high-cycle, corrosion and fretting fatigues of steels in a virgin state and after operation are compared. Salient features of fractures of such steels are revealed.
引用
收藏
页码：449 / 460
页数：12
相关论文
共 50 条
  • [1] A study of different modes of fatigue fracture and durability estimation for compressor disks of gas-turbine engines
    Burago N.G.
    Zhuravlev A.B.
    Nikitin I.S.
    Yakushev V.L.
    Mathematical Models and Computer Simulations, 2016, 8 (5) : 523 - 532
  • [2] Research on Simulation of supercritical steam turbine system in large thermal power station
    Zhou, Qiongyang
    ADVANCES IN MATERIALS, MACHINERY, ELECTRONICS II, 2018, 1955
  • [3] Rehabilitation of a steam turbine at Knepper Power Station
    VGB PowerTech, 4 (37-41):
  • [4] Thermal fatigue of steam turbine in power generation system of waste combined with gas turbine generator
    Kosugi, T
    7TH ISWA INTERNATIONAL CONGRESS, PROCEEDINGS II, 1996, : II192 - II193
  • [5] Conserving electrical energy through steam turbine driven pumps in thermal power station
    Ramanujacharyulu, T.K.
    Irrigation and Power, 1992, 49 (03):
  • [6] GT 26 gas turbine in the combined cycle gas and steam turbine power station: repowering of the Rheinhafen steam power station of Badenwerk AG
    Waller, Von H.
    Scherer, D.
    Scherer, V.
    VGB-Kraftwerkstechnik, 1996, 76 (08): : 626 - 632
  • [7] Corrosion Fatigue Analysis in Power Steam Turbine Blade
    Ramirez, Jose Alfredo Rodrigez
    Mirafuentes, Christian Marisol Clemente
    Garibay, Manuela Alejandra Zalapa
    Castrejon, Juan Garcia C.
    Anaya, Luis Gonzalo Guillen
    METALS, 2023, 13 (03)
  • [8] Comparative Evaluation of Resistance to Brittle Fracture of Steels for Steam Turbine Disks.
    Chizhik, A.I.
    Rabinovich, V.P.
    Berkman, I.V.
    Genze, A.A.
    Ivanova, I.G.
    Energomashinostroenie, 1977, (04): : 31 - 33
  • [9] NUMERICAL ANALYSIS OF THE STEAM TURBINE PERFORMANCE IN POWER STATION WITH A LOW POWER CYCLE
    Bdaiwi, Mothana
    Akroot, Abdulrazzak
    Wahhab, Hasanain A. Abdul
    Mahariq, Ibrahim
    JOURNAL OF ENGINEERING SCIENCE AND TECHNOLOGY, 2023, : 163 - 177
  • [10] The fatigue and fracture analysis of steam turbine rotor shafts containing defects
    Wang S.
    Wang W.Q.
    Song M.D.
    Zhang H.
    Key Engineering Materials, 2019, 795 : 254 - 261
12345