Tribological properties of laser surface texturing and molybdenizing duplex-treated stainless steel at elevated temperatures

被引:24
|
作者
Li, Jianliang [1 ]
Xiong, Dangsheng [1 ]
Wu, Hongyan [2 ]
Zhang, Yongkang [1 ]
Qin, Yongkun [1 ]
机构
[1] Nanjing Univ Sci & Technol, Sch Mat Sci & Engn, Nanjing 210094, Jiangsu, Peoples R China
[2] Nanjing Univ Informat & Technol, Coll Math & Phys, Nanjing 210044, Jiangsu, Peoples R China
来源
关键词
Double glow plasma surface alloying; Laser surface texturing; Wear resistance; high temperature; CARBON-STEEL; FRICTION; WEAR; LUBRICATION; COATINGS;
D O I
10.1016/j.surfcoat.2012.06.002
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Surface texturing can be used as the storage of solid lubricant. The stainless steel was first laser surface textured and then was molybdenized by double glow plasma alloying technology to improve its tribological properties. The friction and wear properties of texturing and molybdenizing duplex-treated steel from room temperature to 600 degrees C were tested on a ball-on-disk tribometer. The hardness of stainless steel is increased from HV196 to HV480 after molybdenizing. The friction coefficient of textured stainless steel smeared with MoS2 powders decreases from 0.40 to 0.10 at elevated temperature after molybdenizing. The wear rates of texturing and molybdenizing duplex-treated steel are much lower than those of single textured steel at elevated temperatures due to the lubrication of oxides of molybdenum. (C) 2012 Elsevier B.V. All rights reserved.
引用
收藏
页码:S219 / S223
页数:5
相关论文
共 50 条
  • [1] Tribological Properties of Laser Surface Texturing and Molybdenizing Duplex-Treated Ni-Base Alloy
    Li, Jianliang
    Xiong, Dangsheng
    Wu, Hongyan
    Huang, Zhongjia
    Dai, Jihui
    Tyagi, Rajnesh
    [J]. TRIBOLOGY TRANSACTIONS, 2010, 53 (02) : 195 - 202
  • [2] Tribological properties of laser surface texturing and coating duplex-treated surface
    Jiang, Jie
    Xiong, Dang-Sheng
    Li, Jian-Liang
    Shi, Yan
    [J]. ADVANCED STRUCTURAL MATERIALS, 2011, 686 : 706 - 710
  • [3] Corrosion and mechanical properties of duplex-treated 301 stainless steel
    Azzi, M.
    Benkahoul, M.
    Klemberg-Sapieha, J. E.
    Martinu, L.
    [J]. SURFACE & COATINGS TECHNOLOGY, 2010, 205 (05): : 1557 - 1563
  • [4] Structural, mechanical and tribological properties of duplex-treated AISI 5140 steel
    Alsaran, A
    Çelik, A
    Karakan, M
    [J]. MATERIALS CHARACTERIZATION, 2005, 54 (01) : 85 - 92
  • [5] Friction Properties of Laser Surface Texturing and Molybdenum Alloying Duplex-Treated Ni-Based Alloy
    Li, Jianliang
    Xiong, Dangsheng
    [J]. ADVANCED TRIBOLOGY, 2009, : 636 - 637
  • [6] TRIBOLOGICAL BEHAVIOUR OF DUPLEX-TREATED PLASTIC MOLD STEEL
    Alpaslan, O.
    Gunyuz, M.
    Atar, E.
    Cimenoglu, H.
    [J]. JOURNAL OF THE BALKAN TRIBOLOGICAL ASSOCIATION, 2013, 19 (01): : 37 - 43
  • [7] Manipulation of tribological properties of stainless steel by picosecond laser texturing and quenching
    Wang, Zhuo
    Wang, Cheng-Wei
    Wang, Min
    Zhao, Quan-Zhong
    [J]. TRIBOLOGY INTERNATIONAL, 2016, 99 : 14 - 22
  • [8] Angle-dependent lubricated tribological properties of stainless steel by femtosecond laser surface texturing
    Wang, Zhuo
    Li, Yang-Bo
    Bai, Feng
    Wang, Cheng-Wei
    Zhao, Quan-Zhong
    [J]. OPTICS AND LASER TECHNOLOGY, 2016, 81 : 60 - 66
  • [9] Modulation of dry tribological property of stainless steel by femtosecond laser surface texturing
    Wang, Zhuo
    Zhao, Quanzhong
    Wang, Chengwei
    Zhang, Yang
    [J]. APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2015, 119 (03): : 1155 - 1163
  • [10] Modulation of dry tribological property of stainless steel by femtosecond laser surface texturing
    Zhuo Wang
    Quanzhong Zhao
    Chengwei Wang
    Yang Zhang
    [J]. Applied Physics A, 2015, 119 : 1155 - 1163