Investigation of crack initiation and propagation behavior of AISI 310 stainless steel up to very high cycle fatigue

被引：14
|
作者：
Khan, M. K. [1 ]
Wang, Q. Y. [1 ]
机构：
[1] Sichuan Univ, Dept Mech & Engn Sci, Chengdu 610065, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2013年 / 54卷
基金：
中国国家自然科学基金;
关键词：
Very high cycle fatigue; Surface roughness; PSBs; Local plasticity; Crack initiation; GIGACYCLE FATIGUE; SURFACE-RELIEF; BEARING STEEL; MECHANISM; IRON; AFM;
D O I：
10.1016/j.ijfatigue.2013.04.009
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Fatigue behavior up to very high cycles for AISI 310 stainless steel has been investigated. The fatigue crack initiated from the surface of the material. It was found that up to 10(6) cycles, cracks initiated from the carbide precipitates at grain boundaries. However, above 10(6) cycles, the cracks initiated from persistent slip bands found at the surface of the specimen. At lower stress levels, slip bands were developed without initiating the cracks. The horizontal asymptote S-N curve from 10(6) to 10(9) cycles was attributed to the development of slip bands all over the surface of the specimen, before crack initiation. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：38 / 46
页数：9
相关论文
共 50 条
  • [21] Effects of microstructure on crack initiation in super martensitic stainless steel under very-high-cycle fatigue at elevated temperature
    Li, Xue
    He, Chao
    Wang, Xiangyu
    Chen, Yao
    Wang, Chong
    Zhang, Hong
    Li, Lang
    Liu, Yongjie
    Wang, Qingyuan
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2023, 46 (03) : 1060 - 1077
  • [22] The effect of the embrittlement on the fatigue limit and crack propagation in a duplex stainless steel during high cycle fatigue
    Marinelli, M. C.
    Krupp, U.
    Kuebbeler, M.
    Herenu, S.
    Alvarez-Armas, I.
    ENGINEERING FRACTURE MECHANICS, 2013, 110 : 421 - 429
  • [23] Investigations on the fatigue crack propagation threshold in Very High Cycle Fatigue
    Wang, Chong
    Wagner, Daniele
    Bathias, Claude
    11TH INTERNATIONAL FATIGUE CONGRESS, PTS 1 AND 2, 2014, 891-892 : 357 - 362
  • [24] High-Cycle Fatigue Properties and Crack Initiation and Propagation Behavior of 2397 Alloy
    Zheng, Ziqiao (s-maloy@mail.csu.edu.cn), 2017, Science Press (46):
  • [25] High-Cycle Fatigue Properties and Crack Initiation and Propagation Behavior of 2397 Alloy
    Fan Xuesong
    Zheng Ziqiao
    Zhang Long
    Hu Fang
    Gong Zhu
    RARE METAL MATERIALS AND ENGINEERING, 2017, 46 (05) : 1327 - 1333
  • [26] Fatigue crack initiation and propagation of 100Cr6 steel under torsional loading in very high cycle regime
    Xue, Hongqian
    Gao, Tao
    Sun, Zhidan
    Zhang, Xianjie
    12TH INTERNATIONAL FATIGUE CONGRESS (FATIGUE 2018), 2018, 165
  • [27] Effect of microstructure on small fatigue crack initiation and early propagation behavior in super martensite stainless steel
    Li, Xue
    Ye, Tian
    Du, Yaohan
    Zhan, Min
    Wang, Xiangyu
    Dai, Yajun
    Liu, Yongjie
    Wang, Chong
    Yang, Kun
    He, Chao
    Wang, Qingyuan
    International Journal of Fatigue, 2025, 190
  • [28] High cycle fatigue properties and fatigue crack propagation behavior of a bainite railway axle steel
    Zhang, Tianyu
    Wang, Yu
    Zhang, Chi
    Wang, Lingyu
    Di, Hongshuang
    Xu, Wei
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 172
  • [29] Fractography and crack initiation of very-high-cycle fatigue for a high carbon low alloy steel
    Zhou, Cheng'en
    Qian, Gui'an
    Hong, Youshi
    FRACTURE AND DAMAGE MECHANICS V, PTS 1 AND 2, 2006, 324-325 : 1113 - +
  • [30] Effect of main inclusions on crack initiation in bearing steel in the very high cycle fatigue regime
    Chao Gu
    Yan-ping Bao
    Peng Gan
    Min Wang
    Jin-shan He
    International Journal of Minerals,Metallurgy and Materials, 2018, 25 (06) : 623 - 629
12345