Surface porosity investigation of aluminum-silicon PM alloys

被引：6

作者：

Steedman, G. ^{[1
]}

Bishop, D. P. ^{[1
]}

Caley, W. F. ^{[1
]}

Kipouros, G. J. ^{[1
]}

机构：

[1] Dalhousie Univ, Dept Proc Engn & Appl Sci, Mat Engn Program, Halifax, NS B3H 4R2, Canada

来源：

POWDER TECHNOLOGY | 2012年 / 226卷

基金：

加拿大自然科学与工程研究理事会;

关键词：

Surface porosity; Open porosity; Powder metallurgy; Aluminum-silicon alloys; Pycnometry; Surface engineering;

D O I：

10.1016/j.powtec.2012.04.049

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

An alternative method for measuring the surface porosity of pressed and sintered PM alloys was investigated. Materials used for this research consisted of a commercially available alloy. Alumix 231, and a proprietary alloy. DAL 6-Si PM alloys. The densities of the samples of the two alloys were analyzed using helium-pycnometry and oil-impregnation. In both cases, the measured density by helium-pycnometry was found to be 1-2% higher than that determined by the oil impregnation method and closer to the theoretical density. This is believed to be due to the superior ability of helium to penetrate the microstructure of these alloys. In addition, the volume of open (surface) porosity was calculated for both alloys. The results showed significant differences in the volume of open and closed porosity measured by the two techniques. Helium-pycnometry gives higher open porosity values and lower closed porosity compared to oil impregnation method. (C) 2012 Elsevier B.V. All rights reserved.

引用

页码：225 / 230

页数：6

共 50 条

[31] ELEMENTS OF V GROUP AS MODIFIERS OF ALUMINUM-SILICON ALLOYS
PILLAI, NR
ANANTHAR.TR
TRANSACTIONS OF THE METALLURGICAL SOCIETY OF AIME, 1968, 242 (09): : 2025 - &
[32] EXCESS VACANCIES AND NUCLEATION OF PRECIPITATES IN ALUMINUM-SILICON ALLOYS
OZAWA, E
KIMURA, H
ACTA METALLURGICA, 1970, 18 (09): : 995 - &
[33] Density and solidification shrinkage of hypoeutectic aluminum-silicon alloys
Magnusson, T
Arnberg, L
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2001, 32 (10): : 2605 - 2613
[34] Fatigue and creep properties of aluminum-silicon cast alloys
Takigawa, Jun
Keikinzoku Yosetsu/Journal of Light Metal Welding and Construction, 2010, 48 (08): : 10 - 15
[35] Density and solidification shrinkage of hypoeutectic aluminum-silicon alloys
T. Magnusson
L. Arnberg
Metallurgical and Materials Transactions A, 2001, 32 : 2605 - 2613
[36] THE DISSOLUTION OF STRONTIUM-CONTAINING MASTER ALLOYS IN ALUMINUM AND ALUMINUM-SILICON FOUNDRY ALLOYS
PEKGULERYUZ, M
CLOSSET, B
GRUZLESKI, JE
CIM BULLETIN, 1985, 78 (878): : 97 - 97
[37] ALLOYING ALUMINUM-SILICON ALLOYS TO IMPROVE THEIR PROPERTIES.
Stepanov, Yu.N.
Konovalov, Yu.I.
Gulyaev, B.B.
Petrov, S.M.
Shemetev, G.F.
Tsvetnye Metally, 1988, 1 : 66 - 68
[38] STRUCTURAL MODIFICATION OF ALUMINUM-SILICON ALLOYS BY ANTIMONY TREATMENT
NAGEL, G
PORTALIER, R
INTERNATIONAL CAST METALS JOURNAL, 1980, 5 (04): : 2 - 6
[39] TRIBOLOGICAL CHARACTERISTICS OF LEADED ALUMINUM-SILICON BEARING ALLOYS
PATHAK, JP
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 1993, 46 (06): : 377 - 385
[40] HYPEREUTECTIC ALUMINUM-SILICON ALLOYS 390 AND A390
JORSTAD, JL
TRANSACTIONS OF THE METALLURGICAL SOCIETY OF AIME, 1968, 242 (07): : 1217 - &

← 1 2 3 4 5 →