Effect of hygrothermal environment on the fatigue fracture mechanism of single lap Aluminum-CFRP hybrid (riveted/bonded) joints

被引：18
|
作者：
Zhang, Hanyu [1 ,2 ]
Song, Zhouzhou [1 ,2 ]
Zhang, Lei [1 ,2 ]
Liu, Zhao [3 ]
Zhu, Ping [1 ,2 ]
机构：
[1] Shanghai Jiao Tong Univ, State Key Lab Mech Syst & Vibrat, Shanghai 200240, Peoples R China
[2] Shanghai Jiao Tong Univ, Natl Engn Res Ctr Automot Power & Intelligent Cont, Shanghai 200240, Peoples R China
[3] Shanghai Jiao Tong Univ, Sch Design, Shanghai 200240, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2022年 / 165卷
基金：
中国国家自然科学基金; 上海市自然科学基金;
关键词：
CFRP; Aluminum alloy; Hybrid joint; Fatigue fracture mechanism; Hygrothermal environment; LIFE PREDICTION; BEHAVIOR; STRENGTH; DAMAGE; MODEL; PERFORMANCE; COMPOSITES; WATER;
D O I：
10.1016/j.ijfatigue.2022.107177
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Due to being composed of different materials, Aluminum-CFRP hybrid (riveted/bonded) joints (HJs) exhibit different fatigue failure modes under different loading and environmental conditions. This paper investigates the influence of hygrothermal environment on the fatigue fracture mechanism of HJs through experimental and simulation researches. Experiments demonstrate the multi-stage character of HJs' fatigue failure with dissimilar failure sequence behavior under different hygrothermal environments and fatigue load conditions. Particularly, through numerical analysis, the competitive mechanism of HJs' fatigue failure behavior has been first revealed to explain the possible fracture modes of the HJs under different fatigue loading and aging conditions.
引用
收藏
页数：20
相关论文
共 50 条
  • [41] Numerical analysis of dynamic response: Fatigue behaviour analysis of Al alloy-CFRP riveted single-shear lap joints
    Wang, He
    Li, Hechang
    Fan, Jianfei
    Liu, Xuetong
    Peng, Jinfang
    He, Liping
    Liu, Jianhua
    Zhu, Minhao
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 170
  • [42] A novel method for damage analysis of CFRP single-lap bolted, bonded and hybrid joints under compression
    Zhang, Hongzhuang
    Li, Changyou
    Xu, Mengtao
    Liu, Zhendong
    Jia, Dawei
    Zhang, Yimin
    COMPOSITE STRUCTURES, 2020, 251
  • [43] Effect of sealing treatment on mechanical properties of CFRP-Aluminum alloy single lap joints
    Chen, Hongli
    Wang, Dengfeng
    Na, Jingxin
    Chen, Xin
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2022, 119
  • [44] Effect of hygrothermal and thermal aging on the fatigue and static strength of mechanical and hybrid single lap joint
    Karimi, Sajjad
    Nasab, Mehran Rezvani
    Afshari, Roham
    Alaei, Mohmmad Hossein
    COMPOSITE STRUCTURES, 2023, 309
  • [45] Modelling the static and fatigue behavior of hybrid spot welded-adhesively bonded single lap joints
    Safaei, Sajjad
    Martulli, Luca Michele
    Bernasconi, Andrea
    Carboni, Michele
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2024, 130
  • [46] Effect of interface non-flatness on the fatigue behavior of adhesively bonded single lap joints
    Razavi, S. M. J.
    Ayatollahi, M. R.
    Samari, M.
    da Silva, L. F. M.
    PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART L-JOURNAL OF MATERIALS-DESIGN AND APPLICATIONS, 2019, 233 (07) : 1277 - 1286
  • [47] Effect of loading rate on the failure of BFRP-Aluminum alloy single lap joints after hygrothermal aging
    Chen, Hongli
    Wang, Dengfeng
    Na, Jingxin
    Chen, Xin
    Zhang, Jicheng
    JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2023, 37 (18) : 2626 - 2641
  • [48] Combined effects of seawater ageing and fatigue loading on the bearing performance and failure mechanism of CFRP/CFRP single-lap bolted joints
    Zhang, Kaifu
    Li, Hailin
    Cheng, Hui
    Luo, Bin
    Liu, Ping
    COMPOSITE STRUCTURES, 2020, 234
  • [49] Quasi-static strength and fatigue life of hybrid (bonded/bolted) composite single-lap joints
    Kelly, G
    COMPOSITE STRUCTURES, 2006, 72 (01) : 119 - 129
  • [50] Fatigue behavior of hybrid multi-bolted-bonded single-lap joints in woven composite plates
    Gamdani, Farid
    Boukhili, Rachid
    Vadean, Aurelian
    INTERNATIONAL JOURNAL OF FATIGUE, 2022, 158
12345