Fatigue and Fatigue Crack Growth Behavior of Tool Steel

被引：0
|
作者：
Sajuri, Z. [1 ]
Syarif, J. [1 ]
Omar, M. Z. [1 ]
Allafi, M. M. [1 ]
Sudar, M. F. [1 ]
机构：
[1] Univ Kebangsaan Malaysia, Dept Mech & Mat Engn, Bangi 43600, Selangor, Malaysia
来源：
PROCEEDINGS OF THE 1ST WSEAS INTERNATIONAL CONFERENCE ON MATERIALS SCIENCE (MATERIALS'08) | 2008年
关键词：
Fatigue; FCG; Inclusion; Stress intensity factor; Life prediction; Tool steel;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Fatigue and fatigue crack growth (FCG) behaviors of tool steel were investigated at room temperature. Fatigue tests were performed under a load control with sinusoidal waveform of stress ratio R=0.1 at a frequency of 10Hz. The fatigue crack was identified nucleated from inclusion presents at specimen surface. The inclusion became the stress raiser and acts as the fatigue fracture origin. The fatigue limit value was observed at 396Mpa. The threshold stress intensity factor range obtained from the fatigue crack growth test was 8.06MPam(1/2). The fatigue crack growth curve was then used to predict the fatigue life based on modified Paris equation. The predicted lives were in good agreement with the experimental results.
引用
收藏
页码：53 / 56
页数：4
相关论文
共 50 条
  • [1] Fatigue Crack Growth Behavior of Eutectoid Steel Rail
    Yaodong Cen
    Lin Chen
    Chunjiao Ji
    Huijun Wang
    Xirong Bao
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2022, 37 : 507 - 512
  • [2] Fatigue Crack Growth Behavior of Eutectoid Steel Rail
    Cen Yaodong
    Chen Lin
    Ji Chunjiao
    Wang Huijun
    Bao Xirong
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2022, 37 (03): : 507 - 512
  • [3] Fatigue Crack Growth Behavior of Eutectoid Steel Rail
    岑耀东
    陈林
    JI Chunjiao
    WANG Huijun
    BAO Xirong
    JournalofWuhanUniversityofTechnology(MaterialsScience), 2022, 37 (03) : 507 - 512
  • [4] Effect of surface coating on fatigue life and fatigue crack growth behavior of AISI D2 tool steel
    Masuda, K.
    Ishihara, S.
    Shibata, H.
    Sakamoto, Y.
    Oguma, N.
    Iwasaki, M.
    INTERNATIONAL JOURNAL OF FATIGUE, 2024, 183
  • [5] On the fatigue crack growth behavior of a nitrided and shot peened steel
    Guagliano, M.
    Vergani, L.
    MECHANICAL BEHAVIOR OF MATERIALS X, PTS 1AND 2, 2007, 345-346 : 375 - +
  • [6] Microstructural effects on fatigue crack growth behavior of a microalloyed steel
    Laurito, D. F.
    Baptista, C. A. R. P.
    Torres, M. A. S.
    Abdalla, A. J.
    FATIGUE 2010, 2010, 2 (01): : 1915 - 1925
  • [7] Fatigue crack growth behavior in ultrafine grained low carbon steel
    Kim, HK
    Choi, MI
    Chung, CS
    Shin, DH
    KSME INTERNATIONAL JOURNAL, 2002, 16 (10): : 1246 - 1252
  • [8] Short fatigue crack growth behavior in a ferritic-bainitic steel
    Hussain, K.
    Tauqir, A.
    Hashmi, F.H.
    Khan, A.Q.
    Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 1994, 25 A (11): : 2421 - 2425
  • [9] Competition mechanisms of fatigue crack growth behavior in lath martensitic steel
    Yang, M.
    Zhong, Y.
    Liang, Y. -l.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2018, 41 (12) : 2502 - 2513
  • [10] Fatigue crack growth behavior in stainless steel under cyclic torsion
    Yu, Huichen
    Tanaka, Keisuke
    STRUCTURAL INTEGRITY AND MATERIALS AGEING IN EXTREME CONDITIONS, 2010, : 227 - 232
12345