Effect of Fe on the Precipitate Characteristics and Out-of-pile Corrosion Behavior of Zr-1Nb-xFe Alloys

被引：2
|
作者：
Wang, Rongshan [1 ]
Weng, Likui [1 ]
Zhang, Yanwei [1 ]
Geng, Jianqiao [1 ]
Du, Chenxi [1 ]
Liu, Erwei [1 ]
机构：
[1] Suzhou Nucl Power Res Inst, Met Component Life Assessment Dept, Suzhou 215004, Peoples R China
来源：
ENERGY AND ENVIRONMENT MATERIALS | 2013年 / 743-744卷
关键词：
Zr alloy; Precipitate characteristics; Corrosion behavior; OXIDE CHARACTERISTICS; PHASE; NB; ZR; PARTICLES;
D O I：
10.4028/www.scientific.net/MSF.743-744.1
中图分类号：
TE [石油、天然气工业]; TK [能源与动力工程];
学科分类号：
0807 ; 0820 ;
摘要：
The effects of Fe addition on the precipitate characteristics and out-of-pile corrosion behavior of Zr-1Nb-xFe alloys, with x=0, 0.2 and 0.4 respectively, were investigated. The experimental results showed that the alloy with the composition of Zr-1Nb-0.4Fe had the best corrosion resistance and the alloy with the composition of Zr-1Nb-0.2Fe had the worst corrosion resistance. The relationship between the corrosion behavior and the microstructures including precipitate characteristics was discussed, and the elements contents, area fraction, as well as the mean diameter of the precipitate were analyzed. The beta-Nb precipitate was found in Zr-1Nb alloy, both Zr(Nb,Fe)(2) precipitate and beta-Nb precipitate were formed in Zr-1Nb-0.2Fe alloy, while only Zr(Nb,Fe)(2) precipitate was observed in Zr-1Nb-0.4Fe alloy. It has been found that the size of precipitates increased with the increasing of Fe content. This work indicated that the Fe content dominates the crystal structure, volume fraction and the element contents of the precipitate, which affect the corrosion resistance of Zr alloy.
引用
收藏
页码：1 / 7
页数：7
相关论文
共 50 条
  • [41] EFFECT OF MOLYBDENUM ON THE CORROSION BEHAVIOR OF AMORPHOUS FE-MO-C ALLOYS IN 1-N HCL
    HASHIMOTO, K
    ASAMI, K
    NAKA, M
    MASUMOTO, T
    SCIENCE REPORTS OF THE RESEARCH INSTITUTES TOHOKU UNIVERSITY SERIES A-PHYSICS CHEMISTRY AND METALLURGY, 1979, 27 (02): : 237 - 245
  • [42] Effect of Mn content on the microstructure, mechanical properties and corrosion behavior of Ti-Nb-Zr-Mn alloys processed via spark plasma sintering
    Chen, Bo
    An, Xuguang
    Zhang, Jing
    Li, Haishan
    Cai, Zheng
    Yao, Weitang
    Wang, Qingyuan
    Kong, Qingquan
    VACUUM, 2024, 229
  • [43] Effect of Ar Ion Irradiation on Microstructure and Corrosion Resistance of Zr-0.75Sn-1Nb-0.35Fe-0.15Cr Alloy
    Gu, Zhiyuan
    Wu, Yue
    Lin, Xiaodong
    Yao, Meiyi
    Hu, Lijuan
    Liang, Xue
    Li, Yifeng
    Peng, Jianchao
    Xie, Yaoping
    Zhou, Bangxin
    RARE METAL MATERIALS AND ENGINEERING, 2024, 53 (06) : 1642 - 1653
  • [44] Influence of the corrosion on the saturation magnetic density of amorphous and nanocrystalline Fe73Nb3Si15.5B7.5Cu1 and Fe80Zr3.5Nb3.5B12Cu1 alloys
    Souza, CAC
    May, JE
    Carlos, IA
    de Oliveira, MF
    Kuri, SE
    Kiminami, CS
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2002, 304 (1-3) : 210 - 216
  • [45] Effect of oxygen content in 400 °C super-heated steam on the corrosion resistance of Zr-xSn-0.35Fe-0.15Cr-0.15 Nb alloys
    Xu, Shitong
    Huang, Jiansong
    Pei, Wen
    Yao, Meiyi
    Hu, Lijuan
    Xie, Yaoping
    Lin, Xiaodong
    Liang, Xue
    Peng, Jianchao
    Xu, Jing
    Zhou, Bangxin
    CORROSION SCIENCE, 2022, 198
  • [46] Development of Ti-Zr-Nb-Ta-Ag high entropy alloy for dental implants: In vitro corrosion behavior, antibacterial effect, and surface characteristics
    Hussein, M. A.
    Kumar, A. Madhan
    Azeem, M. A.
    Ankah, N.
    Saravanan, S.
    MATERIALS CHEMISTRY AND PHYSICS, 2025, 329
  • [47] THE EFFECT OF TUNGSTEN ON THE CORROSION BEHAVIOR OF AMORPHOUS FE-CR-W-P-C ALLOYS IN 1M HCL
    HABAZAKI, H
    KAWASHIMA, A
    ASAMI, K
    HASHIMOTO, K
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1991, 138 (01) : 76 - 81
  • [48] Microstructural Evolution Under He+ Irradiation and Its Effect on Corrosion Behavior of Zr-0.75Sn-0.35Fe-0.15Cr-xNb Alloys
    Yi Lisha
    Zhang Xingwang
    Lin Xiaodong
    Yao Meiyi
    Hu Lijuan
    Li Jianjian
    Liang Xue
    Peng Jianchao
    Xie Yaoping
    Zhou Bangxin
    RARE METAL MATERIALS AND ENGINEERING, 2023, 52 (04) : 1328 - 1337
  • [49] Microstructural Evolution Under He+ Irradiation and Its Effect on Corrosion Behavior of Zr-0.75Sn-0.35Fe-0.15Cr-xNb Alloys
    Yi, Lisha
    Zhang, Xingwang
    Lin, Xiaodong
    Yao, Meiyi
    Hu, Lijuan
    Li, Jianjian
    Liang, Xue
    Peng, Jianchao
    Xie, Yaoping
    Zhou, Bangxin
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2023, 52 (04): : 1328 - 1337
  • [50] Corrosion resistance of Zr-0.7Sn-1Nb-0.03Fe-xCu-xGe (x=0, 0.05, 0.2) alloys in superheated steam at 400℃/10.3 MPa
    Tu, Liming
    Zhang, Jinlong
    Xu, Qidi
    Yao, Meiyi
    Zhou, Bangxin
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2015, 44 (06): : 1391 - 1396
12345