Thermal Properties of Green High-Performance Fiber-Reinforced Cementitious Composites Subjected to High Temperature

被引:0
|
作者
Li, Xiuling [1 ]
Zhang, Huining
Chen, Genda
Bao, Yi
机构
[1] Shandong Jianzhu Univ, Sch Civil Engn, Jinan 250101, Peoples R China
来源
关键词
SELF-CONSOLIDATING CONCRETE; ELEVATED-TEMPERATURES; CRACKING;
D O I
暂无
中图分类号
TU [建筑科学];
学科分类号
0813 ;
摘要
To study the influences of mix proportions and high temperature on the thermal properties of green high-performance fiber reinforced cementitious composites (GHPFRCC), sixteen mix proportions were designed using the Taguchi orthogonal method. Five variables investigated were the water-to-binder ratio (0.24, 0.28, 0.32, and 0.36), sand-to-binder ratio (0.36, 0.46, 0.56, and 0.66), polyvinyl alcohol (PVA) fiber content (1.5%, 1.7%, 2.0%, and 2.2%) by volume, fly ash replacement (60%, 65%, 70%, and 75%) by weight, and the superplasticizer content (0.10%, 0.15%, 0.20%, and 0.25%). Each GHPFRCC specimen was subjected to a target temperature (200 degrees C, 400 degrees C, 600 degrees C, and 800 degrees C), and then measured for its thermal conductivity using a transient plane source method. The experimental results showed that the thermal conductivity of GHPFRCC decreased dramatically in the initial stage up to 400 degrees C, then slowly decreased with temperature until 800 degrees C. Compared with normal concrete, the GHPFRCC is relatively low in thermal conductivity and, therefore, can be used as a better thermal insulation material for infrastructures.
引用
收藏
页码:309 / 315
页数:7
相关论文
共 50 条
  • [1] Creep and shrinkage of high-performance fiber-reinforced cementitious composites
    Rouse, Jon M.
    Billington, Sarah L.
    [J]. ACI MATERIALS JOURNAL, 2007, 104 (02) : 129 - 136
  • [2] Study on the Seismic Behavior of Green High-performance Fiber-reinforced Cementitious Composites Column
    Li, Xiuling
    Luo, Min
    [J]. ADVANCED BUILDING MATERIALS AND SUSTAINABLE ARCHITECTURE, PTS 1-4, 2012, 174-177 : 806 - 809
  • [3] Review of using glass in high-performance fiber-reinforced cementitious composites
    Guo, Pengwei
    Bao, Yi
    Meng, Weina
    [J]. CEMENT & CONCRETE COMPOSITES, 2021, 120
  • [4] Tension and Cyclic Behavior of High-Performance Fiber-Reinforced Cementitious Composites
    Khlef, Feras L.
    Barbosa, Andre R.
    Ideker, Jason H.
    [J]. JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2019, 31 (10)
  • [5] Residual Tensile Properties and Explosive Spalling of High-Performance Fiber-Reinforced Cementitious Composites Exposed to Thermal Damage
    Park, Gang-Kyu
    Park, Gi-Joon
    Park, Jung-Jun
    Lee, Namkon
    Kim, Sung-Wook
    [J]. MATERIALS, 2021, 14 (07)
  • [6] Bond behavior and interface modeling of reinforced high-performance fiber-reinforced cementitious composites
    Bandelt, Matthew J.
    Frank, Timothy E.
    Lepech, Michael D.
    Billington, Sarah L.
    [J]. CEMENT & CONCRETE COMPOSITES, 2017, 83 : 188 - 201
  • [7] Strain Softening of High-Performance Fiber-Reinforced Cementitious Composites in Uniaxial Compression
    Kwon, Seung-Hee
    Lee, Jung-Soo
    Koh, Kyungtaek
    Kim, Hyeong-Ki
    [J]. INTERNATIONAL JOURNAL OF CONCRETE STRUCTURES AND MATERIALS, 2024, 18 (01)
  • [8] Strain Softening of High-Performance Fiber-Reinforced Cementitious Composites in Uniaxial Compression
    Seung-Hee Kwon
    Jung-Soo Lee
    Kyungtaek Koh
    Hyeong-Ki Kim
    [J]. International Journal of Concrete Structures and Materials, 18
  • [9] Experimental dataset on the residual performance of fiber-reinforced cementitious composite subjected to high temperature
    Soares Jr, Paulo Roberto Ribeiro
    Maciel, Priscila de Souza
    Correa, Elaine Carballo Siqueira
    Bezerra, Augusto Cesar da Silva
    [J]. DATA IN BRIEF, 2022, 45
  • [10] Influence of carbon fiber on the electromagnetic shielding effectiveness of high-performance fiber-reinforced cementitious composites
    Park, Gijoon
    Kim, Sungwook
    Park, Gang-Kyu
    Lee, Namkon
    [J]. JOURNAL OF BUILDING ENGINEERING, 2021, 35