Electrical property of semiconducting (Ba,Sr)TiO3 ceramics with the microstructure controlled by heating rate

被引:4
|
作者
Suzuki, R
Ogino, K
Sato, K
Suzuki, T
机构
[1] Central Research Laboratory, Japan Energy Co., Ltd., Toda-shi, Saitama 335, 3-17-35, Niizo-Minami
关键词
semiconducting; (Ba; Sr); TiO3; heating rate; grain size; specific resistivity; PTCR effect; breakdown voltage;
D O I
10.2109/jcersj.105.391
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Semiconducting (Ba0.9Sr0.1) TiO3 ceramics with 0.1mol% Sb2O3 and 0.05 mol% Ta2O5 were prepared by changing sintering temperature and heating rate. Microstructure, specific resistivity at room temperature, magnitude of PTCR effect and breakdown voltage of the obtained ceramics were investigated. Abnormal grain growth was observed from 1300 degrees C and became remarkable at the temperature regime between 1320 degrees C and 1360 degrees C. The specific resistivity at room temperature decreased and the magnitude of PTCR effect increased with increasing the degree of abnormal grain growth. When the heating rate is increased from 180 degrees C/h to 500 degrees C/h at the temperature regime between 1300 degrees C and 1360 degrees C, the grain size of the samples decreased from 44 mu m to 18 mu m. The specific resistivity at room temperature increased from 5 Omega cm to 7.5 Omega cm by decreasing average grain size. However, both the magnitude of PTCR effect and the resistivity in the grain evaluated by the complex impedance measurement were independent of the grain size, The breakdown voltage increased from 31 V/mm to 60 V/mm with decreasing the grain size from 44 mu m to 18 mu m, There was the linear relationship between the breakdown voltage and the reverse of the grain size, and the breakdown voltage of a grain boundary was estimated 0.78 V from the slope of this relationship. In this study, it was revealed that the heating rate is one of the critical factors for properties of (Ba, Sr) TiO3 ceramics. Rapid heating at a proper temperature regime is a preferable condition for the ceramics with fine microstructure, which results in the improvement of their breakdown voltage without significant increase of the specific resistivity at room temperature.
引用
收藏
页码:391 / 394
页数:4
相关论文
共 50 条
  • [1] Microstructure and electrical properties of porous (Ba,Sr)TiO3 ceramics
    Park, K
    Kim, JG
    Kim, J
    Cho, WS
    [J]. MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2002, 88 (01): : 9 - 13
  • [2] CO-FIRING OF SEMICONDUCTING (BA,SR)TIO3 AND (BA,PB)TIO3 CERAMICS
    HO, IC
    HSIEH, HL
    [J]. JOURNAL OF MATERIALS SCIENCE LETTERS, 1993, 12 (23) : 1829 - 1830
  • [3] Fabrication and microstructure evolution of sandwiched (Ba,Sr)TiO3 ceramics
    Wang, Tingting
    Jin, Dengren
    Yang, Wu
    Cheng, Jinrong
    [J]. CURRENT APPLIED PHYSICS, 2011, 11 (03) : S208 - S212
  • [4] Microstructure-property relationships of (Ba,Sr)TiO3 films
    Waser, R
    Hoffmann, S
    [J]. JOURNAL OF THE KOREAN PHYSICAL SOCIETY, 1998, 32 : S1340 - S1343
  • [5] FABRICATION OF MULTILAYER BARRIER LAYER CAPACITORS WITH SEMICONDUCTING (BA,SR)TIO3 CERAMICS
    ITOH, T
    TASHIRO, S
    IGARASHI, H
    [J]. JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS, 1993, 32 (9B): : 4261 - 4264
  • [6] The Role of Microstructure on Microwave Dielectric Properties of (Ba,Sr)TiO3 Ceramics
    Song, Zhe
    Xu, Qi
    Zhang, Shujun
    Liu, Hanxing
    Luo, Wei
    Hao, Hua
    Cao, Minghe
    Yao, Zhonghua
    Hu, Wei
    Shi, Yatong
    Lanagan, Michael T.
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2016, 99 (03) : 905 - 910
  • [7] Solidification behavior and microstructure of (Ba,Sr) TiO3 ceramics prepared by aerodynamic levitation
    Lee, Ki-Ju
    Lee, Chi-Hoon
    Jung, Sang-Kyo
    Lee, Gye-Hyeok
    Cho, Won-Seung
    Hwang, Woon-Suk
    [J]. JOURNAL OF CERAMIC PROCESSING RESEARCH, 2017, 18 (01): : 45 - 50
  • [8] Effects of (Ba, Sr)TiO3 film thickness on electrical properties of (Ba, Sr)TiO3/(Ba, Sr)RuO3 capacitor
    Oh, SH
    Park, KW
    Park, JH
    Kim, BS
    Choi, DK
    [J]. JOURNAL OF VACUUM SCIENCE & TECHNOLOGY B, 2000, 18 (04): : 1923 - 1928
  • [9] INFLUENCE OF BALL MILLING TIME ON THE PTCR EFFECT IN POROUS SEMICONDUCTING (BA, SR)TIO3 CERAMICS
    LIANG, R
    KUWABARA, M
    [J]. NIPPON SERAMIKKUSU KYOKAI GAKUJUTSU RONBUNSHI-JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1989, 97 (06): : 645 - 648
  • [10] VARISTOR CHARACTERISTICS OF (BA,SR)TIO3 SEMICONDUCTING CERAMICS FIRED IN REDUCING-REOXIDIZING ATMOSPHERE
    ISHIYA, T
    TASHIRO, S
    IGARASHI, H
    [J]. JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS, 1995, 34 (9B): : 5309 - 5312