A new double layer oxidation resistant coating based on Er2SiO5/LaMgAl11O19 deposited on C/SiC composites by atmospheric plasma spraying

被引：32

作者：

Zou, Binglin ^{[1
]}

Khan, Zuhair S. ^{[1
,3
]}

Fan, Xizhi ^{[1
,4
]}

Huang, Wenzhi ^{[1
,4
]}

Gu, Lijian ^{[1
,4
]}

Wang, Ying ^{[1
,4
]}

Xu, Jiaying ^{[1
,4
]}

Tao, Shunyan ^{[2
]}

Yang, Kuiyue ^{[1
]}

Ma, Hongmei ^{[1
]}

Cao, Xueqiang ^{[1
]}

机构：

[1] Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Rare Earth Resources Utilizat, Changchun 130022, Peoples R China

[2] Chinese Acad Sci, Shanghai Inst Ceram, Key Lab Inorgan Coating Mat, Shanghai 200050, Peoples R China

[3] Natl Univ Sci & Technol, Ctr Energy Syst, Islamabad, Pakistan

[4] Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China

来源：

SURFACE & COATINGS TECHNOLOGY | 2013年 / 219卷

关键词：

C/SiC composites; Coating; Oxidation; Thermal cycling; Failure mechanism; ENVIRONMENTAL BARRIER COATINGS; YTTRIUM SILICATE COATINGS; MATRIX COMPOSITES; ROOM-TEMPERATURE; SIC COMPOSITES; PROTECTION; BEHAVIOR; DURABILITY; FAILURE;

D O I：

10.1016/j.surfcoat.2013.01.011

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A new coating with Er2SiO5 as inner layer and LaMgAl11O19 (LMA) as top layer was designed and deposited on C/SiC composites by atmospheric plasma spraying to improve the oxidation resistance of the substrate at high temperature. Microstructure, oxidation protection and failure mechanism of the Er2SiO5/LMA coating during dynamic thermal cycling (DTC) were investigated. The results showed that a good interfacial bonding between the substrate and the coating was present before and after DTC test. Weight loss for the sample coated on one-side was 4.5% after 11 cycles of heating for 85 min, and for the uncoated sample was as high as 20.6%. Failure mechanism of the coating resulted from the liquid sintering of the coating and the formation of bubbles between the substrate and the coating. (c) 2013 Elsevier B.V. All rights reserved.

引用

页码：101 / 108

页数：8

共 22 条

[21] ZrB2-SiC-Ta4HfC5/Ta4HfC5 Oxidation-Resistant Dual-Layer Coating Fabricated by Spark Plasma Sintering for C/C Composites
Zhou, Changling
Qi, Yushi
Cheng, Yehong
Han, Wenbo
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (01) : 512 - 518
[22] Synthesis and characterization of Yb and Er based monosilicate powders and durability of plasma sprayed Yb2SiO5 coatings on C/C-SiC composites
Khan, Zuhair S.
Zou, Binglin
Huang, Wenzhi
Fan, Xizhi
Gu, Lijian
Chen, Xiaolong
Zeng, Shuibing
Wang, Chunjie
Cao, Xueqiang
MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2012, 177 (02): : 184 - 189

← 1 2 3 →