Modelling plastic deformation of metals over a wide range of strain rates using irreversible thermodynamics

Based on the theory of irreversible thermodynamics, the present work proposes a dislocation-based model to describe the plastic deformation of FCC metals over wide ranges of strain rates. The stress-strain behaviour and the evolution of the average dislocation density are derived. It is found that there is a transitional strain rate (similar to 10(4) s(-1)) over which the phonon drag effects appear, resulting in a significant increase in the flow stress and the average dislocation density. The model is applied to pure Cu deformed at room temperature and at strain rates ranging from 10(-5) to 10(6) s(-1) showing good agreement with experimental results.