Synthesis and Characterization of Nano Co0.6Fe0.4S2

被引：0
|
作者：
Sharma, Pooja [1 ]
Razia, N. [1 ]
机构：
[1] Univ Rajasthan, Dept Phys, Jaipur 302004, Rajasthan, India
来源：
SOLID STATE PHYSICS, VOL 57 | 2013年 / 1512卷
关键词：
Superparamagnetism; nanoparticles; magnetization;
D O I：
10.1063/1.4791010
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
The synthesis and characterization of nano Co0.6Fe0.4S2 was reported. Characterization of the sample was done using X-Ray Diffraction and Scanning Electron Microscopy. XRD results show the sample to be of amorphous nature with average particle size raning from 5.56 nm to 7.01 nm. Stoichiometry of the sample was ensured through X-Ray Fluorescence and EDAX measurements. Field variation of magnetization measurement further supports formation of nanoparticles.
引用
收藏
页码：260 / 261
页数：2
相关论文
共 50 条
  • [1] Synthesis and characterization of Co0.4 Fe0.6 thin film alloy
    Mohanta, Maheswari
    Parida, S. K.
    Sahoo, Ananya
    Gupta, Mukul
    Medicherla, V. R. R.
    MATERIALS TODAY-PROCEEDINGS, 2021, 35 : 82 - 85
  • [2] Metal vacancies abundant Co0.6Fe0.4S2 on N-doped porous carbon nanosheets as anode for high performance lithium batteries
    Wang, Guangming
    Yue, Hailong
    Xu, Yakun
    Jin, Rencheng
    Wang, Qingyao
    Gao, Shanmin
    Jin, Rencheng (jinrc427@126.com), 1600, Elsevier Ltd (330):
  • [3] Metal vacancies abundant Co0.6Fe0.4S2 on N-doped porous carbon nanosheets as anode for high performance lithium batteries
    Wang, Guangming
    Yue, Hailong
    Xu, Yakun
    Jin, Rencheng
    Wang, Qingyao
    Gao, Shanmin
    ELECTROCHIMICA ACTA, 2020, 330
  • [4] Polyaniline/Co0.6Zn0.4Fe2O4 core-shell nano-composites. Synthesis, characterization and properties
    Gabal, M. A.
    Al-Juaid, A. A.
    El-Rashed, S.
    Hussein, M. A.
    Al Angari, Y. M.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 747 : 83 - 90
  • [5] Polyaniline/Co0.6Zn0.4Fe2O4 core-shell nano-composites. Synthesis, characterization and properties
    Gabal, M.A. (mgabalabdonada@yahoo.com), 1600, Elsevier Ltd (747):
  • [6] Characterization and synthesis of Ni0.6Zn0.4(Fe2O4)1 nano-particles using
    Li, Qiao-ling
    Ye, Yun
    Wang, Yong-fei
    Jing, Hong-xia
    Wang, Ya-kun
    ADVANCES IN COMPOSITE MATERIALS AND STRUCTURES, PTS 1 AND 2, 2007, 334-335 : 993 - +
  • [7] Large Magnetoresistance Effect in Epitaxial Co2Fe0.4Mn0.6Si/Ag/Co2Fe0.4Mn0.6Si Devices
    Sato, Jo
    Oogane, Mikihiko
    Naganuma, Hiroshi
    Ando, Yasuo
    APPLIED PHYSICS EXPRESS, 2011, 4 (11)
  • [8] Fabrication of fully epitaxial Co2Cr0.6Fe0.4Al/MgO/Co2Cr0.6Fe0.4Al magnetic tunnel junctions
    Marukame, T.
    Ishikawa, T.
    Hakamata, S.
    Matsuda, K-I
    Uemura, T.
    Yamamoto, M.
    IEEE TRANSACTIONS ON MAGNETICS, 2007, 43 (06) : 2782 - 2784
  • [9] Synthesis and microwave absorbing property of the dendritic Fe0.6Co0.4 alloy
    Tian, Liangliang
    Wang, Fei
    OPTOELECTRONICS AND ADVANCED MATERIALS-RAPID COMMUNICATIONS, 2013, 7 (9-10): : 688 - 691
  • [10] Perpendicular magnetic anisotropy in Co2Fe0.4Mn0.6Si
    Ludbrook, B. M.
    Ruck, B. J.
    Granville, S.
    JOURNAL OF APPLIED PHYSICS, 2016, 120 (01)
12345