Effect of Mg on the sintering of Al-Mg alloy powders by pulse electric-current sintering process

被引：48
|
作者：
Xie, GQ [1 ]
Ohashi, O
Sato, T
Yamaguchi, N
Song, MH
Mitsuishi, K
Furuya, K
机构：
[1] Natl Inst Mat Scci, Nanocharacterizat Grp, Nanomat Lab, Tsukuba, Ibaraki 3050003, Japan
[2] Niigata Univ, Grad Sch Sci & Technol, Niigata 9502181, Japan
来源：
MATERIALS TRANSACTIONS | 2004年 / 45卷 / 03期
关键词：
deoxidization; pulse electric-current sintering; aluminium-magnesium alloy; oxide film; resistivity; tensile strength;
D O I：
10.2320/matertrans.45.904
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Utilization of deoxidization mechanism of magnesium (Mg) is an effective method to remove the oxide films at aluminum (Al) alloy powder surface in pulse electric-current sintering (PECS) process. The continuous amorphous oxide film at Al alloy surface are broken and removed by deoxidization of Mg. Crystalline particles of MgAl2O4 or MgO, or both of them, are formed, which depend on Mg content in Al alloy powder and sintering temperature. After that the metal/metal contact is caused, and solid state sintering of Al alloy powder is facilitated. The electrical resistivity and tensile properties of powder compacts are improved by Mg addition. Based on the analyses of electrical resistivity, tensile properties and microstructures of the sintered specimens, optimum amount of Mg addition to improve the sintering properties of Al powder is determined to be 0.3-2.5 mass%.
引用
收藏
页码：904 / 909
页数：6
相关论文
共 50 条
  • [31] Effect of fluctuating temperature field on the sintering of Al-10Mg alloy
    Zhang, W. X.
    Chai, D. L.
    Lin, Y.
    Xi, Y. L.
    Zhou, J. E.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 459 (1-2) : 433 - 437
  • [32] PROCESS OF ALLOY FORMING IN THE POWDER SYSTEM AL-MG
    SAVITSKII, AP
    TIMOFEEV, NS
    MARTSUNOVA, LS
    ZHDANOV, VV
    PAVLOVA, LA
    SOVIET POWDER METALLURGY AND METAL CERAMICS, 1990, 29 (08): : 608 - 611
  • [33] Selective laser sintering/melting (SLS/SLM) of pure Al, Al-Mg, and Al-Si powders: Effect of processing conditions and powder properties
    Olakanmi, E. O.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2013, 213 (08) : 1387 - 1405
  • [34] Effect of Mg on sintering phenomenon of aluminum alloy powder
    Kondoh, Katsuyoshi
    Kimura, Atsushi
    Watanabe, Ryuzo
    Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy, 2000, 47 (01): : 36 - 41
  • [35] Manufacturing of porous magnesium alloy by pulse electric current sintering process and their compressive properties
    Okumura, H
    Watanabe, K
    Kamado, S
    Kojima, Y
    MAGNESIUM ALLOYS 2003, PTS 1 AND 2, 2003, 419-4 : 1019 - 1024
  • [36] Thermally stable nanocrystalline Al-Mg alloy powders produced by cryomilling
    Zhou, F
    Rodriguez, R
    Lavernia, EJ
    METASTABLE, MECHANICALLY ALLOYED AND NANOCRYSTALLINE MATERIALS, 2002, 386-3 : 409 - 414
  • [37] The Formation of Morphologies and Microstructures in Electrodeposited Nanocrystalline Al-Mg Alloy Powders
    Tatiparti, Sankara Sarma V.
    Ebrahimi, Fereshteh
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2010, 157 (10) : E167 - E171
  • [38] Refinement of the grain size and electric mechanism of Al-Mg alloy
    Zhou, Dianwu
    Liu, Jinshui
    Yang, Feng
    Li, Guifa
    Chen, Lu
    Peng, Ping
    Tezhong Zhuzao Ji Youse Hejin/Special Casting and Nonferrous Alloys, 2006, 26 (02): : 115 - 118
  • [39] Potentiostatic versus galvanostatic electrodeposition of nanocrystalline Al-Mg alloy powders
    Sarma, Sankara
    Tatiparti, V.
    Ebrahimi, Fereshteh
    JOURNAL OF SOLID STATE ELECTROCHEMISTRY, 2012, 16 (03) : 1255 - 1262
  • [40] Effects of on/off pulse pattern on sintering alumina by a pulsed electric current sintering process
    Dang, Khanh Quoc
    Nanko, Makoto
    JOURNAL OF CERAMIC PROCESSING RESEARCH, 2009, 10 : S32 - S38
12345