Fabrication of Al-LiAlO2 metal matrix composites and crystalline γ-LiAlO2

被引：5
|
作者：
Li, T. K. [1 ]
Ng, Dickon H. L. [1 ]
机构：
[1] Chinese Univ Hong Kong, Dept Phys, Shatin, Hong Kong, Peoples R China
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2007年 / 445卷
关键词：
metal matrix composites; lithium alummate; powder metallurgy;
D O I：
10.1016/j.msea.2006.09.092
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
We report the synthesis of nano-structured LiAlO2 network in an Al-based metal matrix composite (MMC) by sintering a powder compact of Al-15 wt.%Li2O. The morphology of the in situ formed network in the Al matrix was similar in all the samples prepared at temperatures between 300 degrees C and the arc-melting temperature. However, it was found that the LiAlO2 was initially amorphous when the MMC sample was prepared at temperatures below similar to 700 degrees C, but it would be completely converted to crystalline gamma-phase LiAlO2 by sintering at 1000 degrees C. The MMCs had made nano-porous by removing the Al matrix with NaOH solution. The sizes of pores were determined to be about 130-230 nm and the width of the branches of the gamma-phase lithium aluminate (gamma-LiAlO2) network were about 50-100 nm. (c) 2006 Elsevier B.V. All rights reserved.
引用
收藏
页码：652 / 656
页数：5
相关论文
共 50 条
  • [41] MOCVD growth of GaN on LiAlO2(100) substrates
    Xu, K
    Xu, J
    Deng, PZ
    Qiu, RS
    Fang, ZJ
    PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1999, 176 (01): : 589 - 593
  • [42] A new high-pressure phase of LiAlO2
    Li, XJ
    Kobayashi, T
    Zhang, FX
    Kimoto, K
    Sekine, T
    JOURNAL OF SOLID STATE CHEMISTRY, 2004, 177 (06) : 1939 - 1943
  • [43] Growth and characterization of GaN on LiGaO2 and LiAlO2
    Duan, SK
    Teng, XG
    Han, PD
    Lu, DC
    BLUE LASER AND LIGHT EMITTING DIODES II, 1998, : 158 - 161
  • [44] Wet chemical etching of LiGaO2 and LiAlO2
    Hsu, CH
    Ip, KP
    Johnson, JW
    Chu, SNG
    Kryliouk, O
    Pearton, SJ
    Li, L
    Chai, BHT
    Anderson, TJ
    Ren, F
    ELECTROCHEMICAL AND SOLID STATE LETTERS, 2001, 4 (06) : C35 - C38
  • [45] γ-LiAlO2晶体的生长缺陷研究
    杨卫桥
    干福熹
    邓佩珍
    徐军
    李杼智
    蒋成勇
    人工晶体学报, 2002, (06) : 565 - 568
  • [46] Effect of the Reaction Medium on the Mechanochemical Synthesis of LiAlO2
    Isupov, V. P.
    Bulina, N. V.
    Borodulina, I. A.
    INORGANIC MATERIALS, 2018, 54 (02) : 147 - 155
  • [47] Mechanochemical synthesis of fine-particle γ-LiAlO2
    V. P. Isupov
    Ya. E. Trukhina
    N. V. Eremina
    N. V. Bulina
    I. A. Borodulina
    Inorganic Materials, 2016, 52 : 1189 - 1197
  • [48] Growth studies of GaN and alloys on LiAlO2 by MOVPE
    Dikme, Y
    van Gemmern, P
    Chai, B
    Hill, D
    Szymakowski, A
    Kalisch, H
    Heuken, M
    Jansen, RH
    PHYSICA STATUS SOLIDI C - CONFERENCES AND CRITICAL REVIEWS, VOL 2, NO 7, 2005, 2 (07): : 2161 - 2165
  • [49] Mechanochemical synthesis of fine-particle γ-LiAlO2
    Isupov, V. P.
    Trukhina, Ya. E.
    Eremina, N. V.
    Bulina, N. V.
    Borodulina, I. A.
    INORGANIC MATERIALS, 2016, 52 (11) : 1189 - 1197
  • [50] Sweep gas chemistry effect on vaporization of LiAlO2
    Suzuki, A
    Yamawaki, M
    Yasumoto, M
    Yamaguchi, K
    JOURNAL OF NUCLEAR MATERIALS, 1996, 233 : 1452 - 1456
12345