Anisotropy Affecting Dendrite Growth of Fe-C Alloy in a Forced Flow

被引:1
|
作者
Yuan, Xunfeng [1 ]
Liu, Baoying [1 ]
机构
[1] Shangluo Univ, Dept Phys & Elect Informat Engn, Shangluo 726000, Peoples R China
关键词
Phase-field; Forced flow; Dendrite growth; Anisotropy; BINARY ALLOY; PHASE;
D O I
10.4028/www.scientific.net/AMM.268-270.352
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The phase-field model coupling with the concentration field and flow field was used to simulate the dendrite growth during isothermal solidification of Fe-C alloy in a forced flow. The effects of anisotropy modulus and anisotropy strength on the dendrite growth are studied. The results indicate that the dendrites have four preferential growth orientation and the side-branches growth is not perpendicular to the primary branch while the dendrite along with < 100 > crystallographic directions. When the dendrite along with < 110 > crystallographic directions, the dendrites have six preferential growth orientation and the side-branches are parallel to the neighborly primary branch. At a anisotropy strength of 0.01, the crystal have no apparent principal branch and grows into coral shapes. With an increase in anisotropy strength, the tip solute concentration decreases, makes the dendrite growth become fast, the tip velocity increased continuously.
引用
收藏
页码:352 / 355
页数:4
相关论文
共 50 条
  • [41] Dissolution rate of solid iron into liquid Fe-C alloy
    Minsoo Shin
    Joon Seok Oh
    Jeoungho Lee
    Sukkwang Jung
    Joonho Lee
    Metals and Materials International, 2014, 20 : 1139 - 1143
  • [42] Optimization of bath composition for hard Fe-C alloy plating
    Fujiwara, Y
    Izaki, M
    Enomoto, H
    Nagayama, T
    Yamauchi, E
    Nakae, A
    JOURNAL OF APPLIED ELECTROCHEMISTRY, 1998, 28 (08) : 855 - 862
  • [43] The structure of liquid Fe-C alloy near the melting point
    Luo, J
    Zhai, QJ
    Zhao, P
    Qin, XB
    CANADIAN METALLURGICAL QUARTERLY, 2004, 43 (02) : 177 - 181
  • [44] FACTORS CONTROLLING CARBIDE DISTRIBUTION DENSITY IN FE-C ALLOY
    ABE, M
    TAKAHASHI, N
    AKISUE, O
    KATOH, H
    USHIODA, K
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1983, 23 (07) : B265 - B265
  • [45] Substructure and crystallography of degenerate pearlite in an Fe-C binary alloy
    Furuhara, T.
    Moritani, T.
    Sakamoto, K.
    Maki, T.
    THERMEC 2006, PTS 1-5, 2007, 539-543 : 4832 - +
  • [46] Dissolution Rate of Solid Iron into Liquid Fe-C Alloy
    Shin, Minsoo
    Oh, Joon Seok
    Lee, Jeoungho
    Jung, Sukkwang
    Lee, Joonho
    METALS AND MATERIALS INTERNATIONAL, 2014, 20 (06) : 1139 - 1143
  • [47] SEPARATED EUTECTIC IN THE SOLIDIFICATION OF FE-C ALLOY WITH ELECTROMAGNETIC STIRRING
    CAO, ZQ
    REN, ZM
    ZHANG, LP
    JIN, JZ
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1992, 11 (23) : 1579 - 1581
  • [48] Simulation of lamellar pearlite growth in Fe-C system
    Svoboda, J
    Sopousek, J
    HIGH TEMPERATURE MATERIALS CHEMISTRY, PTS I AND II, PROCEEDINGS, 2000, 15 : 217 - 220
  • [49] NUCLEATION AND GROWTH OF PROEUTECTOID FERRITE IN FE-C AND FE-C-X ALLOYS
    ENOMOTO, M
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1984, 70 (14): : 1648 - 1658
  • [50] Estimation of primary dendrite arm spacing and solidified interface morphology in low carbon steel by introducing quasi Fe-C binary alloy
    Esaka, H
    Ogibayashi, S
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1998, 84 (01): : 49 - 54