Ion implantation as a tool to study the oxidation behaviour of TiAl-based intermetallics

被引：25
|
作者：
Stroosnijder, MF [1 ]
Schmutzler, HJ [1 ]
Haanappel, VAC [1 ]
Sunderkotter, JD [1 ]
机构：
[1] COMMISS EUROPEAN COMMUNITIES, JOINT RES CTR, INST ADV MAT, I-21020 ISPRA, ITALY
来源：
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION | 1997年 / 48卷 / 01期
关键词：
D O I：
10.1002/maco.19970480108
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
TiAl-based intermetallic alloys are being considered as structural materials for high-temperature applications due to their low density and substantial mechanical strength at high temperatures. The effect of various elements added by ion implantation on the oxidation behaviour of near-gamma Ti-48Al-2Cr and Ti-48Al-2Cr-2Nb (compositions are given in at-%) in air at 800 degrees C has been studied. Ions implanted (10(17) ions/cm(2)) were Al, Ti, Cr, Mo, Y, Mn, Pt, Nb, and Si in case of Ti-48Al-2Cr and Nb in case of Ti-48Al-2Cr-2Nb. Comparison was made with the oxidation behaviour of Ti-48Al-2Cr-2Nb and Ti-47Al-2Cr-0.2Si alloys in which quaternary elements were added by alloying. It is concluded that ion implantation can serve as a research tool to study, in the frame of screening tests, the influence of various elements on the corrosion behaviour of materials.
引用
收藏
页码：40 / 47
页数：8
相关论文
共 50 条
  • [41] Influence of niobium ion implantation on the oxidation behaviour of TiAl under thermal cycle conditions
    Taniguchi, S
    Uesaki, K
    Zhu, YC
    Zhang, HX
    Shibata, T
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 249 (1-2): : 223 - 232
  • [42] Improving the oxidation resistance of TiAl-based alloy by siliconizing
    Liang, W
    Zhao, XG
    SCRIPTA MATERIALIA, 2001, 44 (07) : 1049 - 1054
  • [43] Creep behaviour of a cast TiAl-based alloy for industrial applications
    Lapin, J
    INTERMETALLICS, 2006, 14 (02) : 115 - 122
  • [44] Oxidation resistance of ion-implanted γ-TiAl-base intermetallics
    Lei, MK
    Zhu, XP
    Wang, XJ
    OXIDATION OF METALS, 2002, 58 (3-4): : 361 - 374
  • [45] Influence of oxygen on solidification behaviour of cast TiAl-based alloys
    Zollinger, J.
    Lapin, J.
    Daloz, D.
    Combeau, H.
    INTERMETALLICS, 2007, 15 (10) : 1343 - 1350
  • [46] Oxidation Resistance of Ion-Implanted γ-TiAl-Base Intermetallics
    M.K. Lei
    X.P. Zhu
    X.J. Wang
    Oxidation of Metals, 2002, 58 : 361 - 374
  • [47] High-Temperature Oxidation Behaviour of a TiAl-Based Alloy Subjected to Aluminium Hot-Dipping
    D. Pilone
    A. Mondal
    L. Zortea
    Oxidation of Metals, 2022, 98 : 529 - 543
  • [48] Development of a Nb-free TiAl-based intermetallics with a low-temperature superplasticity
    Qiu, Congzhang
    Liu, Yong
    Zhang, Wei
    Liu, Bin
    Hang, Xiaopeng
    INTERMETALLICS, 2012, 27 : 46 - 51
  • [49] High-Temperature Oxidation Behaviour of a TiAl-Based Alloy Subjected to Aluminium Hot-Dipping
    Pilone, D.
    Mondal, A.
    Zortea, L.
    OXIDATION OF METALS, 2022, 98 (5-6): : 529 - 543
  • [50] Oxidation behavior of a γ-TiAl-based alloy implanted by silicon and/or carbon
    Li, XY
    Taniguchi, S
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 398 (1-2): : 268 - 274
12345