High loading LiFePO4 on activated carbon fiber cloth as a high capacity cathode for Li-ion battery

The LiFePO4/carbon fiber (LFP/CF) cathodes were prepared by using activated carbon fiber cloth as current collector in place of conventional Al foil. The electrochemical properties of LFP/CF electrodes were analyzed by the cyclic voltammetry and galvanostatic charge/discharge tests. The results indicate that the activated carbon fiber cloth with high specific surface area and high porosity makes the LFP/CF electrode that possesses higher mass loading of 18-21 mg cm(-2) and stronger redox reaction ability compared with Al foil-based electrode. The LFP/CF electrode shows excellent rate performance and cycle stability. At 0.1C, the discharge capacity is up to 190.1 mAh g(-1) that exceeds the theoretical capacity due to the combination effect of battery and capacitor. Furthermore, the LFP/CF electrode shows an initial capacity of 150.4 mAh g(-1) at 1C with a capacity retention of 74.7% after 425 cycles, which is higher than 62.4% for LFP/Al foil electrode, and an initial discharge capacity of 130 mAh g(-1) at 5C with a capacity retention of 61.5% after 370 cycles. But this composite electrode is not suitable for charging/discharging at higher rate as 10C due to too much mass loading.