Comparison of damages in tungsten and tungsten doped with lanthanum-oxide exposed to dense deuterium plasma shots

被引：28

作者：

Shirokova, V. ^{[1
]}

Laas, T. ^{[1
]}

Ainsaar, A. ^{[1
]}

Priimets, J. ^{[1
]}

Ugaste, Ue ^{[1
]}

Demina, E. V. ^{[2
]}

Pimenov, V. N. ^{[2
]}

Maslyaev, S. A. ^{[2
]}

Dubrovsky, A. V. ^{[2
,3
]}

Gribkov, V. A. ^{[2
,4
]}

Scholz, M. ^{[4
]}

Mikli, V. ^{[5
]}

机构：

[1] Tallinn Univ, Inst Math & Nat Sci, EE-200108 Tallinn, Estonia

[2] Russian Acad Sci, AA Baikov Inst Met & Mat Sci IMET, Moscow, Russia

[3] Moscow Phys Soc, Moscow, Russia

[4] Inst Plasma Phys & Laser Microfus, Warsaw, Poland

[5] Tallinn Univ Technol, Fac Chem & Mat Technol, Tallinn, Estonia

来源：

JOURNAL OF NUCLEAR MATERIALS | 2013年 / 435卷 / 1-3期

关键词：

PULSED ION; FOCUS; STREAMS;

D O I：

10.1016/j.jnucmat.2012.12.027

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Changes in the surface and structure of tungsten and tungsten doped with 1% lanthanum-oxide samples irradiated by powerful deuterium plasma shots are investigated. Comparative analysis of the samples microroughness, the damage factor estimated from SEM images, and the hardness of cross-sections has been carried out. It can be concluded that the doping of tungsten with 1% lanthanum-oxide may decrease the development of a mesh of microcracks on the irradiated surface. However, this doping may increase the microroughness of the sample surface. (C) 2013 Elsevier B.V. All rights reserved.

引用

页码：181 / 188

页数：8

共 50 条

[31] Damages of carbon-tungsten samples under influence of deuterium ions and dense plasma streams within plasma-focus facility
Gribkov, V. A.
Grebenschikova, Ye. S.
Demina, Ye. V.
Dubrovsky, A. V.
Kovtun, A. V.
Makeev, O. N.
Mahnowski, K.
Maslayev, S. A.
Pimenov, V. N.
Paduch, M.
Rogozhkin, S. V.
Sadowski, M. J.
Skladnik-Sadowska, E.
Scholz, M.
Zaluzhnij, A. G.
PLASMA 2007, 2008, 993 : 361 - +
[32] Dependence of blistering and deuterium retention on damage depth in damaged tungsten exposed to deuterium plasma
Wang, Shiwei
Guo, Wangguo
Cheng, Long
Schwarz-Selinger, Thomas
Liu, Mi
Zhu, Xiuli
Yuan, Yue
Fu, Engang
Lu, Guang-Hong
NUCLEAR FUSION, 2021, 61 (05)
[33] DEUTERIUM TRAPPING AND SPUTTERING OF TUNGSTEN COATINGS EXPOSED TO LOW-ENERGY DEUTERIUM PLASMA
Tolstolutskaya, G. D.
Kuprin, A. S.
Nikitin, A., V
Kopanets, I. E.
Voyevodin, V. N.
Kolodiy, I., V
Vasilenko, R. L.
Ilchenko, A., V
PROBLEMS OF ATOMIC SCIENCE AND TECHNOLOGY, 2020, (02): : 54 - 59
[34] Erosion and deuterium retention behavior of tungsten exposed to impurity-seeded deuterium plasma
Hong Zhang
Han-Wen Zhang
Li Qiao
Xue-Xi Zhang
Ran He
Peng Wang
Tungsten, 2021, 3 (04) : 448 - 458
[35] Erosion and deuterium retention behavior of tungsten exposed to impurity-seeded deuterium plasma
Zhang, Hong
Zhang, Han-Wen
Qiao, Li
Zhang, Xue-Xi
He, Ran
Wang, Peng
TUNGSTEN, 2021, 3 (04) : 448 - 458
[36] Erosion and deuterium retention behavior of tungsten exposed to impurity-seeded deuterium plasma
Hong Zhang
Han-Wen Zhang
Li Qiao
Xue-Xi Zhang
Ran He
Peng Wang
Tungsten, 2021, 3 : 448 - 458
[37] The deuterium depth profile in neutron-irradiated tungsten exposed to plasma
Shimada, Masashi
Cao, G.
Hatano, Y.
Oda, T.
Oya, Y.
Hara, M.
Calderoni, P.
PHYSICA SCRIPTA, 2011, T145
[38] Deuterium trapping in rolled polycrystalline tungsten exposed to low energy plasma
Rusinov, Aleksandr
Sakamoto, Mizuki
Zushi, Hideki
Ohyama, Ryohei
Honda, Koichiro
Takagi, Ikuji
Tanabe, Tetsuo
Yoshida, Naoaki
Plasma and Fusion Research, 2012, 7 (2012):
[39] Blister formation on rough and technical tungsten surfaces exposed to deuterium plasma
Manhard, Armin
Balden, Martin
von Toussaint, Udo
NUCLEAR FUSION, 2017, 57 (12)
[40] Surface modification of tungsten and tungsten-tantalum alloys exposed to high-flux deuterium plasma and its impact on deuterium retention
Zayachuk, Y.
't Hoen, M. H. J.
van Emmichoven, P. A. Zeijlmans
Terentyev, D.
Uytdenhouwen, I.
van Oost, G.
NUCLEAR FUSION, 2013, 53 (01)

← 1 2 3 4 5 →