Influence of mode of electrodeposition, current density and saccharin on the microstructure and hardness of electrodeposited nanocrystalline nickel coatings

被引：108

作者：

Wasekar, Nitin P. ^{[1
]}

Haridoss, Prathap ^{[2
]}

Seshadri, S. K. ^{[2
]}

Sundararajan, G. ^{[1
,2
]}

机构：

[1] Int Adv Res Ctr Powder Met & New Mat, Hyderabad 500005, Andhra Pradesh, India

[2] IITM, Dept Met & Mat Engn, Madras 600036, Tamil Nadu, India

来源：

SURFACE & COATINGS TECHNOLOGY | 2016年 / 291卷

关键词：

Electrodeposition; Nickel; Sulfur; Grain size; Hardness; Texture; GRAIN-SIZE; PULSE; SULFUR; ELECTROCRYSTALLIZATION; SURFACE; GROWTH; CHARGE; DC;

D O I：

10.1016/j.surfcoat.2016.02.024

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The main purpose of the present work is to study the influence of current density, deposition mode and the presence of saccharin as an additive on the microstructure, sulfur content, grain size and microhardness of nanocrystalline Ni coatings. Towards this purpose, nanocrystalline nickel (Ni) coatings were deposited at various current densities in Watt's bath using direct, pulse and pulse reverse current (PRC) electrodeposition and subsequently characterized for sulfur content, grain size and hardness. It was observed that, the current density has no influence on the grain size/hardness of nanocrystalline Ni coatings in direct and pulsed current electrodeposition mode. However, the grain size increased from similar to 20 to similar to 200 nm with decrease in current density in PRC mode of deposition. In addition a substantial change in microstructure and texture of PRC Ni coatings was also evident. The experimental results have been rationalized based on the adsorption-desorption type of mechanism during electrodeposition. (C) 2016 Elsevier B.V. All rights reserved.

引用

页码：130 / 140

页数：11

共 50 条

[21] A Galvanostatic Modeling for Preparation of Electrodeposited Nanocrystalline Coatings by Control of Current Density
Ali Mohammad Rashidi
[J]. Journal of Materials Science & Technology, 2012, 28 (12) : 1071 - 1076
[22] A Galvanostatic Modeling for Preparation of Electrodeposited Nanocrystalline Coatings by Control of Current Density
Rashidi, Ali Mohammad
[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2012, 28 (12) : 1071 - 1076
[23] Effect of temperature on the evolution of diffusivity, microstructure and hardness of nanocrystalline nickel films electrodeposited at low temperatures
Chung, C. K.
Chang, W. T.
Chen, C. F.
Liao, M. W.
[J]. MATERIALS LETTERS, 2011, 65 (03) : 416 - 419
[24] MICROSTRUCTURE AND GROWTH OF ELECTRODEPOSITED NANOCRYSTALLINE NICKEL FOILS
CZIRAKI, A
FOGARASSY, B
GEROCS, I
TOTHKADAR, E
BAKONYI, I
[J]. JOURNAL OF MATERIALS SCIENCE, 1994, 29 (18) : 4771 - 4777
[25] Microstructure and growth of electrodeposited nanocrystalline nickel foils
[J]. 1600, (Chapman & Hall Ltd, London, Engl):
[26] Microstructure and thermal stability of electrodeposited nanocrystalline nickel
Hourai, M
Holdway, P
Cerezo, A
Smith, GDW
[J]. METASTABLE, MECHANICALLY ALLOYED AND NANOCRYSTALLINE MATERIALS, 2002, 386-3 : 397 - 402
[27] HARDNESS CONTROL IN ELECTRODEPOSITED NICKEL-PHOSPHORUS COATINGS
NARAYAN, R
MUNGOLE, MN
[J]. METAL FINISHING, 1985, 83 (01) : 55 - 57
[28] Effect of bath additives on the microstructure, lattice defect density and hardness of electrodeposited nanocrystalline Ni films
Kolonits, Tamas
Jenei, Peter
Peter, Laszlo
Bakonyi, Imre
Czigany, Zsolt
Gubicza, Jen
[J]. SURFACE & COATINGS TECHNOLOGY, 2018, 349 : 611 - 621
[29] Effect of current density and grain refining agents on pulsed electrodeposition of nanocrystalline nickel
Bhardwaj, M.
Balani, K.
Balasubramaniam, R.
Pandey, S.
Agarwal, A.
[J]. SURFACE ENGINEERING, 2011, 27 (09) : 642 - 648
[30] Effect of Pulse Electrodeposition on Properties of Nanocrystalline Nickel Coatings
Sanaeian, Mohammad Reza
Nasirpouri, Farzad
[J]. ULTRAFINE GRAINED AND NANO-STRUCTURED MATERIALS IV, 2014, 829 : 410 - +

← 1 2 3 4 5 →