T-stress for crack paths in test specimens subject to mixed mode loading

被引：45
|
作者：
Shlyannikov, V. N. [1 ]
机构：
[1] Russian Acad Sci, Res Ctr Rower Engn Problems, Kazan 420111, Russia
来源：
ENGINEERING FRACTURE MECHANICS | 2013年 / 108卷
基金：
俄罗斯基础研究基金会;
关键词：
T-stress; Biaxial loading; Mixed mode fracture; Fatigue crack growth; Crack paths; FRACTURE; GROWTH;
D O I：
10.1016/j.engfracmech.2013.03.011
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
Fatigue crack paths for inclined cracks are studied through experiments and computations under different mixed-mode loading. The elaborated theoretical model is applied for modeling crack growth trajectories in common experimental fracture mechanics specimen geometries. For the particular specimen geometries considered, the T-stress distributions are calculated along the curved crack path. It is shown that there is a greater variation of T-stress along the crack trajectories under mixed mode fracture for specimen with different geometries. The experimental data for mixed mode fracture trajectories during crack growth are compared with theoretical predictions. Discrepancies in fatigue crack path have been observed in various specimen configurations. The results presented in this study for fracture specimens seem to indicate the relevance of crack tip constraint parameter, the T-stress, to fatigue crack path behavior that conventional LEFM fails to explain. (c) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：3 / 18
页数：16
相关论文
共 50 条
  • [31] On the influence of T-Stress on photoelastic analysis under pure mode II loading
    Zakeri, Mahnaz
    Colombo, Chiara
    FRATTURA ED INTEGRITA STRUTTURALE, 2008, (03): : 2 - 10
  • [32] Elastic T-stress evaluation from Fe analysis for mode (I) loading in X52 arc of pipe specimens
    Meliani, M. Hadj
    Benarous, M.
    Ghoul, A.
    Azari, Z.
    SOHN INTERNATIONAL SYMPOSIUM ADVANCED PROCESSING OF METALS AND MATERIALS, VOL 2: THERMO AND PHYSICOCHEMICAL PRINCIPLES: IRON AND STEEL MAKING, 2006, : 657 - 657
  • [33] Effect of T-stress and loading rate on crack initiation in rate sensitive plastic materials
    Jayadevan, KR
    Narasimham, R
    Ramamurthy, TS
    Dattaguru, B
    INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2002, 39 (07) : 1757 - 1775
  • [34] Elastic T-stress for cracks in test specimens subjected to non-uniform stress distributions
    Wang, X
    ENGINEERING FRACTURE MECHANICS, 2002, 69 (12) : 1339 - 1352
  • [35] Evaluation of the T-stress in branch crack problem
    Y. Z. Chen
    X. Y. Lin
    International Journal of Fracture, 2010, 161 : 175 - 185
  • [36] T-stress evaluation for curved crack problems
    Y. Z. Chen
    X. Y. Lin
    Acta Mechanica, 2008, 198 : 35 - 50
  • [37] Evaluation of the T-stress in branch crack problem
    Chen, Y. Z.
    Lin, X. Y.
    INTERNATIONAL JOURNAL OF FRACTURE, 2010, 161 (02) : 175 - 185
  • [38] T-stress and its implications for crack growth
    Tong, J
    ENGINEERING FRACTURE MECHANICS, 2002, 69 (12) : 1325 - 1337
  • [39] Polynomial evaluation of stress intensity factors of CNS specimen with an interface crack subject to mixed-mode loading
    Machida, Kenji
    JSME International Journal, Series A: Mechanics and Material Engineering, 1999, 42 (01): : 57 - 65
  • [40] T-stress evaluation for curved crack problems
    Chen, Y. Z.
    Lin, X. Y.
    ACTA MECHANICA, 2008, 198 (1-2) : 35 - 50
12345