Study on EB-PVD zirconia thermal barrier coatings for gas turbine blade protection

被引：13
|
作者：
Gao, Y
Chen, MC
Shi, CX
机构：
[1] Inst Aeronaut Mat, Dept 5, Beijing 100095, Peoples R China
[2] Natl Nat Sci Fdn China, Beijing 100083, Peoples R China
来源：
MATERIALS AND MANUFACTURING PROCESSES | 1999年 / 14卷 / 05期
关键词：
D O I：
10.1080/10426919908914862
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Thermal barrier coatings on hollow turbine blades of DD3 were studied. The DD3 single crystal alloy has excellent mechanical properties, equivalent to that of PWA 1480. The results show that ZrO2 coatings consist of oriented columnar grains. The coating is composed of t', cubic and tetragonal phases and there is an alumina layer at the ZrO2-NiCrAlY alloy interface after aging for 30 min, at 1050 degrees C. No degradation occurred to the EBPVD ceramic coatings after 200 thermal cycles at 1100 degrees C for 10 min., air cooling and 100 hours high temperature oxidation at 1100 degrees C.
引用
收藏
页码：691 / 696
页数：6
相关论文
共 50 条
  • [21] A parametric study of damage initiation and propagation in EB-PVD thermal barrier coatings
    Bhatnagar, Himanshu
    Ghosh, Somnath
    Walter, Mark E.
    [J]. MECHANICS OF MATERIALS, 2010, 42 (01) : 96 - 107
  • [22] DEVELOPMENT AND CHARACTERIZATION OF EB-PVD THERMAL BARRIER COATINGS WITH DIFFERENT CERAMIC MATERIALS FOR TURBINE BLADES
    Korkmaz, Hanifi Eray
    Guven, Gokhan
    Dikbiyik, Alican
    Yucesan, Guven
    Kazmanli, Kursat
    [J]. PROCEEDINGS OF ASME TURBO EXPO 2024: TURBOMACHINERY TECHNICAL CONFERENCE AND EXPOSITION, GT2024, VOL 2, 2024,
  • [23] Damage mechanisms, life prediction, and development of EB-PVD thermal barrier coatings for turbine airfoils
    Strangman, Tom
    Raybould, Derek
    Jameel, Ahsan
    Baker, Wil
    [J]. SURFACE & COATINGS TECHNOLOGY, 2007, 202 (4-7): : 658 - 664
  • [24] Phase transformation in EB-PVD yttria partially stabilized zirconia thermal barrier coatings during annealing
    [J]. Schulz, Uwe, 1600, American Ceramic Soc (83):
  • [25] Thermal property and failure behavior of LaSmZrO thermal barrier coatings by EB-PVD
    Shen, Zaoyu
    Liu, Guanxi
    Zhang, Rujing
    Dai, Jianwei
    He, Limin
    Mu, Rende
    [J]. ISCIENCE, 2022, 25 (04)
  • [26] Possibilities and limits of temperature control in EB-PVD equipment used for the deposition of zirconia thermal barrier coatings
    Lugscheider, E
    Barimani, C
    Doepper, G
    [J]. HIGH TEMPERATURE SURFACE ENGINEERING, 2000, : 85 - 94
  • [27] Phase transformation in EB-PVD yttria partially stabilized zirconia thermal barrier coatings during annealing
    Schulz, U
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2000, 83 (04) : 904 - 910
  • [28] Degradation of EB-PVD thermal barrier coatings caused by CMAS deposits
    Peng, Hui
    Wang, Lu
    Guo, Lei
    Miao, Wenhui
    Guo, Hongbo
    Gong, Shengkai
    [J]. PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2012, 22 (05) : 461 - 467
  • [29] Oxidation-induced failure of EB-PVD thermal barrier coatings
    Tolpygo, VK
    Clarke, DR
    Murphy, KS
    [J]. SURFACE & COATINGS TECHNOLOGY, 2001, 146 : 124 - 131
  • [30] Characterization and evaluation of EB-PVD thermal barrier coatings by impedance spectroscopy
    Zhang, CX
    Liu, FS
    Gong, SK
    Xu, HB
    [J]. PRICM 5: THE FIFTH PACIFIC RIM INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND PROCESSING, PTS 1-5, 2005, 475-479 : 3997 - 4000
12345