Effect of silver addition on the field trapping properties of Gd-Ba-Cu-O bulk superconductors

被引：17
|
作者：
Nariki, S [1 ]
Sakai, N [1 ]
Matsui, M [1 ]
Murakami, M [1 ]
机构：
[1] ISTEC, Superconduct Res Lab, Minato Ku, Tokyo 1050023, Japan
来源：
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS | 2002年 / 378卷
关键词：
melt processing; trapped magnetic field; mechanical property; Ag; Gd-Ba-Cu-O;
D O I：
10.1016/S0921-4534(02)01541-1
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
The effect of Ag addition on the field trapping properties of Gd-Ba-Cu-O bulk samples has been studied. Gd-BaCu-O bulk superconductors 32 turn in diameter were melt textured by varying the amount of AG(2)O the range of 0-30 wt.%. The trapped magnetic field of Ag-free bulk sample was 1.3 T at 77 K. This value could be improved to 1.8-2.0 T with Ag addition of 10-20 wt.%. A further increase in AG(2)O content degraded the field trapping ability. Ag-free bulk Gd-Ba-Cu-O exhibited the trapped field of 3.0 T at 65 K, however, the bulk was fractured at lower temperature. On the other hand, Ag-added bulk Gd-Ba-Cu-O exhibited the high trapped field value of 6.7 T at 55 K. These results indicate that the mechanical strength of the bulk Gd-Ba-Cu-O could be improved with Ag addition. (C) 2002 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：774 / 778
页数：5
相关论文
共 50 条
  • [41] Evaluation of magnetic homogeneities of Gd-Ba-Cu-O bulk superconductors by different Hall probe scanning methods
    Kono, T
    Fukai, H
    Sakai, N
    Nariki, S
    Hirabayashi, I
    Murakami, M
    Koshizuka, N
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2005, 426 : 632 - 638
  • [42] Magnetic levitation and guidance performance of Y-Ba-Cu-O and Gd-Ba-Cu-O bulk superconductors under low ambient pressure
    Zhang, Weifeng
    Deng, Zigang
    Zhang, Yong
    Wang, Hongdi
    Zheng, Jun
    Shi, Yunhua
    Zhou, Difan
    Cardwell, David A.
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2019, 52 (36)
  • [43] Magnetic field distributions of stacked large single domain Gd-Ba-Cu-O bulk superconductors exceeding 140 mm in diameter
    Sakai, N.
    Nariki, S.
    Nishimura, M.
    Miyazaki, T.
    Murakami, M.
    Miryala, M.
    Hirabayashi, I.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2007, 463 (SUPPL.): : 348 - 352
  • [44] Advances in enlargement of melt-textured Gd-Ba-Cu-O superconductors
    Nariki, S.
    Sakai, N.
    Kita, M.
    Fujikura, M.
    Murakami, M.
    Hirabayashi, I.
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2006, 19 (07): : S500 - S505
  • [45] Improvement of Thermal Stability with Alloy Impregnation in Gd-Ba-Cu-O Superconductors for Pulsed Field Magnetization
    Kimura, Y.
    Matsumoto, H.
    Fukai, H.
    Sakai, N.
    Hirabayashi, I.
    Izumi, M.
    Murakami, M.
    7TH EUROPEAN CONFERENCE ON APPLIED SUPERCONDUCTIVITY (EUCAS'05), 2006, 43 : 389 - 392
  • [46] Fracture strength properties of Gd-Ba-Cu-O large single-grain bulk with CeO2 addition
    Murakami, Akira
    Fujimoto, Hiroyuki
    Iwamoto, Akifumi
    ADVANCES IN SUPERCONDUCTIVITY XXIV, 2012, 27 : 160 - 163
  • [47] Evolution of texture in melt-grown Y-Ba-Cu-O and Gd-Ba-Cu-O superconductors
    Gopalan, R
    Singh, AK
    Rajasekharan, T
    JOURNAL OF MATERIALS SCIENCE, 1997, 32 (10) : 2595 - 2598
  • [48] Evolution of texture in melt-grown Y-Ba-Cu-O and Gd-Ba-Cu-O superconductors
    R GOPALAN
    A. K SINGH
    T RAJASEKHARAN
    Journal of Materials Science, 1997, 32 : 2595 - 2598
  • [49] Field trapping capability of melt-processed (Nd-Eu-Gd)-Ba-Cu-O bulk superconductors
    Yamada, T
    Ikuta, H
    Yoshikawa, M
    Yanagi, Y
    Itoh, Y
    Mizutani, U
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 392 : 623 - 627
  • [50] Microstructure of superconducting hetero-joints between single-grained Gd-Ba-Cu-O bulk superconductors
    Gao, Z.
    Congreve, J. V. J.
    Tutt, N.
    Shi, Y.
    Liu, J.
    Grovenor, C. R. M.
    Cardwell, D. A.
    Durrell, J. H.
    Speller, S. C.
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2025, 38 (01):
12345