Microstructures and microwave dielectric properties of Ba4LiNb3O12-BaWO4 composite ceramics

Composite ceramics of (1 -x)Ba4LiNb3O12-xBaWO(4) (x=0.36-0.69) had been synthesized by co-firing the mixtures of Ba4LiNb3O12 and BaWO4 powders. The structures and microwave dielectric properties of the ceramics were studied by XRD, SEM, and TEM. These ceramics consisted of hexagonal Ba4LiNb3O12 and tetragonal BaWO4. The two phases co-existed well in the ceramics, and there was not obvious reaction at interfacial areas among grains. These ceramics had low sintering temperatures and excellent microwave dielectric properties, especially the small temperature coefficients of resonant frequency (iota(f)) and high quality factor (Q x f) values. For composition at x=0.69, the ceramic sintered at 1070 degrees C had Q x f value of 75,500 GHz and iota(f) value of +8.7 ppm/degrees C. (c) 2012 Elsevier B.V. All rights reserved.