Effect of Co doping on the magnetic and DC electrical properties of Mn-Zn nanoferrites

In this study, Cobalt-Manganese-Zinc nanoferrites with the formula CoxMn0.5-xZn0.5Fe2O4 with x = 0.0, 0.1, 0.3, and 0.5 prepared by chemical Co-precipitation method. Then the structure and morphology of the synthesized nanoparticles were characterized by X-ray diffraction (XRD) and transmitting electron microscopy (TEM), respectively. The XRD patterns indicated the formation of single-phased cubic structure of spinel ferrite in nanometer size with no minor phase. The TEM image showed the formation of nanoparticles with average size of about 40 nm and normal size distribution. The magnetic measurements of the nanoparticles were done at room temperature using a vibrating sample magnetometer (VSM). Results exhibited a super-paramagnetic like behavior for some of the samples. DC electrical resistivity measurements were carried out by two-probe technique from 25 to 250 degrees C and showed decreasing of the resistivity with temperature meanwhile passing a transition to form of a peak. The peaks values observed near the Curie temperatures of samples suggest that anomaly behavior can attributed to spin canting associated with the phase transition from para to ferromagnetic state at T-C. (C) 2018 Elsevier B.V. All rights reserved.