Mechanical properties, biosafety, and shearing bonding strength of glass fiber-reinforced PEEK composites used as post-core materials

Objective: To investigate the mechanical properties, biosafety, and shearing bonding strength of glass fibers-reinforced polyether-ether-ketone (PEEK-GF) for post-core materials.Methods: PEEK-GF composites with different glass fiber contents were prepared by extrusion injection and named PEEK-GF30, PEEK-GF40, and PEEK-GF50. Mechanical properties including flexural modulus, flexural strength, Vickers hardness, and compression strength were tested. The cross-sectional morphology was examined using scanning electron microscopy (SEM). Cytotoxicity was studied in vitro with Cell-counting kit-8 (CCK-8). Cell morphology was observed under a microscope. Cell growth on the composites' surfaces was analyzed with DAPI staining. The shearing bonding strength (SBS) of PEEK-GF50 was assessed after applying different pretreatments. Failure modes were evaluated by microscopy. SEM and contact-angle measurements were performed on the surfaces. Statistical analysis was conducted using one-way ANOVA (P < 0.05).Results: The mechanical properties of PEEK-GF composites improved with increased GF content. The PEEK-GF50 group exhibited flexural modulus (17.4 & PLUSMN; 0.5 GPa) close to that of dentin (18.6 GPa) and showed the highest flexural strength (350.0 & PLUSMN; 2.9 MPa), Vickers hardness (47.6 & PLUSMN; 4.5 HV), and compressive strength (264.0 & PLUSMN; 18.0 MPa). The SEM analysis demonstrated that the PEEK matrix combined well with glass fibers. The CCK-8 results confirmed the biosafety of all groups. DAPI staining indicated that cells were growing well on the composites' surface. The sample that was pretreated with sandblasting and plasma showed the highest SBS (16.0 & PLUSMN; 1.7 MPa). Significance: The PEEK-GF composites demonstrated excellent mechanical properties, biosafety, and SBS, and have great potential to serve as post-core materials.