Effect of Mo on the high-temperature oxidation behavior of Cr-Ni-Mo hot-work die steels

被引：8

作者：

Zhang, Cheng ^{[1
,2
,3
,5
]}

Zhang, Yuqi ^{[1
,2
]}

Hu, Jinmeng ^{[1
,2
]}

Wang, Zhou ^{[1
,2
]}

Xue, Jun ^{[4
]}

Yu, Hua ^{[1
,2
,3
]}

Zhang, Cheng ^{[1
,2
,3
,5
]}

Wang, Xiaodong ^{[1
,2
]}

Cai, Qiaochu ^{[4
]}

Wang, Changji ^{[1
,2
,3
]}

Jiang, Tao ^{[1
,2
]}

Wei, Shizhong ^{[1
,2
,3
]}

Pan, Kunming ^{[1
,2
,3
]}

机构：

[1] Henan Univ Sci & Technol, Natl Joint Engn Res Ctr Abras Control & Molding Me, Luoyang, Peoples R China

[2] Henan Univ Sci & Technol, Sch Mat Sci & Engn, Longmen Lab, Luoyang, Peoples R China

[3] Longmen Lab, Luoyang 471003, Henan, Peoples R China

[4] 208 Res Inst China Ordnance Ind, Beijing 102202, Peoples R China

[5] Univ Sci & Technol Beijing, State Key Lab Adv Met & Mat, 30 Xueyuan Rd, Beijing 10003, Peoples R China

来源：

CORROSION SCIENCE | 2023年 / 224卷

关键词：

Cr-Ni-Mo hot-work die steels; High temperature oxidation behavior; Synergy mechanism; Passivation film; FERRITIC STAINLESS-STEEL; OXIDE LAYERS; WEAR; ALLOY; RESISTANCE; IRON; SPECTROSCOPY; MECHANISM; CATALYSTS; SPECTRA;

D O I：

10.1016/j.corsci.2023.111487

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

To investigate the effect of molybdenum (Mo) on the high-temperature oxidation behavior of low-carbon hotwork die steels in a Cr-Ni-Mo system, five 3Cr3MoxNiW steels were prepared. The addition of Mo resulted in a decrease in the grain size of the 3Cr3MoxNiW steel, as well as an improvement in its oxidation resistance. The addition of Mo to 3Cr3MoxNiW steel reduces the inward diffusion of oxygen and the outward diffusion of iron, which accelerates the formation of chromium oxide. The oxide of Mo can then also participate in the process of protective oxide film formation, thus improving its oxidation resistance.

引用

页数：13

共 50 条

[31] Corrosion cracking of cast Cr-Ni-Mo ferritic-austenitic steels
Melekhov, R. K.
Radkevych, O. I.
Chumalo, H. V.
Yurkevych, R. M.
MATERIALS SCIENCE, 2005, 41 (05) : 686 - 692
[32] Assessment of Cavitation Erosion of Gas-Nitrided Cr-Ni-Mo Steels
Mitelea, Ion
Ghera, Cristian
Bordeasu, Ilare
Craciunescu, Corneliu
JOURNAL OF TRIBOLOGY-TRANSACTIONS OF THE ASME, 2018, 140 (06):
[33] Effect of Silicon on Thermal Stability of 4Cr3Mo2V Hot-Work Die Steel
Li, Ling
Cai, ZhuWen
Wu, XiaoChun
METALS, 2023, 13 (01)
[34] Analysis of fine sulfide inclusions on fracture surfaces of Cr-Ni-Mo steels
Lepekhina, L.I.
Kolokolov, E.I.
Podrezov, N.N.
Viktorov, N.A.
Podrezova, I.S.
Industrial laboratory, 1988, 53 (10): : 914 - 917
[35] EFFECT OF HEAT-TREATMENT IN VACUUM ON CORROSION-RESISTANCE OF CR-NI-MO STEELS
SHCHESNO, LP
EREMENKO, AS
TARABAN, AI
METAL SCIENCE AND HEAT TREATMENT, 1978, 20 (5-6) : 498 - 499
[36] Short-term creep behavior of a Cr Mo V hot-work tool steel
Wurmbauer, Harald
Leitner, Harald
Panzenboeck, Michael
Scheu, Christina
Clemens, Helmut
INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2009, 100 (08) : 1066 - 1073
[37] Effect of isothermal tempering time and temperature on microstructure and hardness of 3Cr5Mo2SiVN hot-work die steel
Wang, Haijian
Feng, Hao
Li, Huabing
Zhang, Shucai
Zhu, Hongchun
Jiang, Zhouhua
MATERIALS CHARACTERIZATION, 2024, 212
[38] ANALYSIS OF FINE SULFIDE INCLUSIONS ON FRACTURE SURFACES OF CR-NI-MO STEELS
LEPEKHINA, LI
KOLOKOLOV, EI
PODREZOV, NN
VIKTOROV, NA
PODREZOVA, IS
INDUSTRIAL LABORATORY, 1987, 53 (10): : 914 - 917
[39] Effect of Ni on the microstructure evolution of Cr-Ni-Mo series high strength weld metal
Peng, Yun, 1600, Harbin Research Institute of Welding (35):
[40] High temperature oxidation behavior of porous Ni-Cr-Mo-Cu materials
Wen Y.
Yang J.-S.
Zhang C.
Zou H.-R.
Fan Y.-Q.
Xiong L.-Q.
Ye J.-P.
Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2022, 32 (08): : 2284 - 2296

← 1 2 3 4 5 →