Influence of Charge Materials on the Metallurgical Quality of Gray Cast Iron

被引：1
|
作者：
Dwulat, R. [1 ,2 ]
Janerka, K. [2 ]
Grzesiak, K. [1 ]
Galuszka, M. [2 ]
机构：
[1] Foundry Lisie Katy, Lisie Katy 7, PL-86302 Grudziadz, Poland
[2] Silesian Tech Univ, Dept Foundry Engn, Towarowa 7, PL-44100 Gliwice, Poland
来源：
ARCHIVES OF FOUNDRY ENGINEERING | 2023年 / 23卷 / 02期
关键词：
Gray cast iron; Thermal analysis; Cast iron properties; Charge materials; Cast iron inoculation;
D O I：
10.24425/afe.2023.144297
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The article presents the influence of the percentage share of pig iron and steel scrap on the chemical composition, physicochemical and mechanical properties. Using an induction furnace, 6 melts were carried out with a variable amount of pig iron in the charge from 0 to 50%. For carburizing, a RANCO 9905 carburizer with a carbon content of 99.2% was used. After melting and introducing FeSi75, temperature measurement was carried out and the metal was superheated to 1500 degrees C. The next step was to pour the samples for chemical analysis, DTA (Derivation Thermal Analysis) and strength and hardness from the melting furnace without inoculation. The last step was to carry out the inoculation by introducing 0.3% barium inoculant into the vat and pouring samplers for DTA analysis. The inoculation was carried out solely to determine changes in DTA parameters, mainly Temin, compared to castings without inoculation.
引用
收藏
页码：66 / 71
页数：6
相关论文
共 50 条
  • [21] Influence of alloying elements on as-cast microstructure and strength of gray iron
    Xu, W
    Ferry, M
    Wang, Y
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 390 (1-2): : 326 - 333
  • [22] Computer-Simulation-Based Estimation of the Quality of a Standard Cast Sample of Gray Cast Iron
    Baron, A. A.
    Palatkina, L., V
    Palatkin, S., V
    RUSSIAN METALLURGY, 2022, 2022 (01): : 35 - 41
  • [23] Improving the quality of iron ore materials in metallurgical enterprises of Russia
    Puzanov, VP
    Malygin, AV
    Boranbaev, BM
    METALLURGIST, 1995, 39 (9-10) : 169 - 169
  • [24] Influence of vanadium and chromium additions on the wear resistance of a gray cast iron
    A.Hassani
    A.Habibollahzadeh
    S.Sadeghinejad Materials
    InternationalJournalofMineralsMetallurgyandMaterials, 2012, 19 (07) : 602 - 607
  • [25] Influence of vanadium and chromium additions on the wear resistance of a gray cast iron
    A. Hassani
    A. Habibollahzadeh
    S. Sadeghinejad
    International Journal of Minerals, Metallurgy, and Materials, 2012, 19 : 602 - 607
  • [26] Influence of SiC and FeSi as silicon carriers on the characteristics of gray cast iron
    Edalati, K
    Akhlaghi, F
    Edalati, A
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2006, 59 (01): : 65 - 72
  • [27] Influence of vanadium and chromium additions on the wear resistance of a gray cast iron
    Hassani, A.
    Habibollahzadeh, A.
    Sadeghinejad, S.
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2012, 19 (07) : 602 - 607
  • [28] Computer-Simulation-Based Estimation of the Quality of a Standard Cast Sample of Gray Cast Iron
    A. A. Baron
    L. V. Palatkina
    S. V. Palatkin
    Russian Metallurgy (Metally), 2022, 2022 : 35 - 41
  • [29] Influence of Shot Peening on Cavitation Erosion Resistance of Gray Cast Iron
    Park, Il-Cho
    CORROSION SCIENCE AND TECHNOLOGY-KOREA, 2021, 20 (03): : 143 - 151
  • [30] Fracture Toughness of Cast Iron - 1: Gray Cast Iron.
    Wolfensberger, Stefan
    Uggowitzer, Peter
    Speidel, Markus O.
    1600, (39):
12345