Broadband 1.0 μm emission in Nd3+/Yb3+co-doped phosphate glasses and fibers for photonic applications

In this work, the spectroscopic properties of 1.0 mu m emission in Nd3+/Yb3+ co-doped phosphate glasses were systematically investigated under 808 nm excitation. Notably, broadband 1.0 mu m emission with a full width at half maximum (FWHM) of 96 nm was obtained in the phosphate glass doped with 2 mol.% Nd2O3 and 1 mol.% Yb2O3. In addition, the energy transfer microscopic parameter and transfer efficiency were analyzed. What is more, multimaterial fibers with Nd3+/Yb3+ co-doped phosphate glass core and silicate cladding were successfully drawn by using the molten core method. An intense 1.0 mu m amplified spontaneous emission (ASE) can be realized in a 3 cm long multimaterial fiber. More importantly, the FWHM of the ASE can reach as large as 60 nm when excited at 976 nm. These results demonstrate that the Nd3+/Yb3+ co-doped phosphate glasses and fibers are promising gain materials for amplifier and laser applications in photonics.(c) 2023 Optica Publishing Group