Enhanced Yield of Large-Sized Ti3C2Tx MXene Polymers Nanosheets via Cyclic Ultrasonic-Centrifugal Separation

Water pollution has spurred the development of membrane separation technology as a potential means of solving the issue. In contrast to the irregular and asymmetric holes that are easily made during the fabrication of organic polymer membranes, forming regular transport channels is essential. This necessitates the use of large-size, two-dimensional materials that can enhance membrane separation performance. However, some limitations regarding yield are associated with preparing large-sized MXene polymer-based nanosheets, which restrict their large-scale application. Here, we propose a combination of wet etching and cyclic ultrasonic-centrifugal separation to meet the needs of the large-scale production of MXene polymers nanosheets. It was found that the yield of large-sized Ti3C2Tx MXene polymers nanosheets reached 71.37%, which was 2.14 times and 1.77 times higher than that prepared with continuous ultrasonication for 10 min and 60 min, respectively. The size of the Ti3C2Tx MXene polymers nanosheets was maintained at the micron level with the help of the cyclic ultrasonic-centrifugal separation technology. In addition, certain advantages of water purification were evident due to the possibility of attaining the pure water flux of 36.5 kg m(-2) h(-1) bar(-1) for the Ti3C2Tx MXene membrane prepared with cyclic ultrasonic-centrifugal separation. This simple method provided a convenient way for the scale-up production of Ti3C2Tx MXene polymers nanosheets.