Mossbauer Investigation of Mn-Doped La-Sr Ferrite Synthesized by the Sol-Gel Method

La0.8Sr0.2Fe1-xMnxO3 (x = 0.0, 0.1, 0.3 and 0.5) series samples were prepared by sol-gel method and characterized by powder X-ray diffractometer (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and Mossbauer spectroscopy. The effects of Mn doping on the microstructure, morphology and electronic structure of La-Sr ferrite were investigated. The XRD results show that all samples are single phase and have orthorhombic structures with Pbnm space group. The surface morphology and composition of chemical elements of the samples were analyzed by SEM and EDS, and the experimental values were consistent with the expected values. The sample was tested by Fe-57 Mossbauer spectroscopy at room temperature, and the results showed that the percentage of doublet increased gradually with the increase of Mn ion doping ratio, and at x = 0.5, all the sextet disappeared and only the doublet existed. According to the analysis, it can be seen that the prepared series of samples underwent a transition from antiferromagnetic to paramagnetic.