Effect of wood moisture content and adhesive open time on the adhesion strength of wet bonded Pinus radiata wood

被引：0
|
作者：
Favis, Jesse [1 ]
Balboni, Bruno Monteiro [1 ]
Wessels, C. Brand [1 ]
机构：
[1] Stellenbosch Univ, Dept Forest & Wood Sci, Stellenbosch, South Africa
来源：
EUROPEAN JOURNAL OF WOOD AND WOOD PRODUCTS | 2024年 / 82卷 / 02期
关键词：
Bond strength (materials) - Glues - Gluing - Moisture - Moisture determination;
D O I：
10.1007/s00107-024-02050-w
中图分类号：
S7 [林业];
学科分类号：
0829 ; 0907 ;
摘要：
Gluing wood in the wet state can reduce warping, splitting, and increase processing volume recovery. Adhesive open time and moisture content may play an important role in bond line strength, but there are no specifications for wet wood bonding. Wood specimens at two different moisture contents were glued with three polyurethane adhesives and tested in shear on the bond line. Open time of 15 min was superior to 4 and 40 min. All adhesives performed better when wood was glued at 30% moisture content than at 101%, but only the 15- and 40-min open time met the minimum shear requirement.
引用
收藏
页码：557 / 560
页数：4
相关论文
共 50 条
  • [21] THE EFFECT OF NITROGEN AND COPPER ON CHARACTERISTICS OF WOOD TISSUE IN PINUS-RADIATA
    DOWNES, GM
    TURVEY, ND
    CANADIAN JOURNAL OF FOREST RESEARCH-REVUE CANADIENNE DE RECHERCHE FORESTIERE, 1990, 20 (09): : 1369 - 1377
  • [22] The effect of wood extractive content on glue adhesion and surface wettability of wood
    Nussbaum, RM
    Sterley, M
    WOOD AND FIBER SCIENCE, 2002, 34 (01): : 57 - 71
  • [23] Effect of moisture content on fracture toughness of wood
    Prokopski, G.
    1997, Polish Academy of Sciences, Warszawa, Poland (43)
  • [24] The effect of temperature and moisture content on drilling resistance measurements in wood (Pinus sylvestris L.)
    Sharapov, Evgenii
    Korolev, Aleksandr
    Demakov, Yury
    WOOD MATERIAL SCIENCE & ENGINEERING, 2024,
  • [25] Improving the adhesion strength and moisture resistance of poly(vinyl acetate) latex as wood adhesive via blending with gelatin
    Morsi, Samir M. M.
    Hussein, Ahmed I.
    Zhou, Xiaojian
    Abd El-Sayed, Essam
    Essawy, Hisham A.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2024, 132
  • [26] Wood stiffness and bending strength in relation to density in four native provenances of Pinus radiata
    Burdon, R.D.
    Britton, R.A.J.
    Walford, G.B.
    New Zealand Journal of Forestry Science, 2001, 31 (01) : 130 - 146
  • [27] Strength of adsorption of polyethylene glycol on pretreated Pinus radiata wood and consequences for enzymatic saccharification
    Vaidya, Alankar A.
    Newman, Roger H.
    Campion, Sylke H.
    Suckling, Ian D.
    BIOMASS & BIOENERGY, 2014, 70 : 339 - 346
  • [28] Effect of moisture on fracture toughness of composite/wood bonded interfaces
    Qiao, PZ
    Davalos, JF
    Trimble, BS
    FATIGUE AND FRACTURE MECHANICS: 31ST VOL, 2000, 1389 : 526 - 544
  • [29] Bonding strength of wood materials bonded with different adhesive after aging test
    Uysal, Burhanettin
    Kurt, Seref
    Yildirim, Mehmet Nuri
    CONSTRUCTION AND BUILDING MATERIALS, 2010, 24 (12) : 2628 - 2632
  • [30] Shear Strength of Eucalyptus saligna Wood Joints Bonded with Polyvinyl Acetate Adhesive
    Biazzon, Joao C.
    Lima Jr, Mauri P.
    Munis, Rafaele A.
    De Araujo, Victor A.
    Morales, Elen A. M.
    Goncalves, Marcos T. T.
    Bueno, Marcus A. P.
    Moizes, Fabio A.
    Leite, Sueli S.
    Salvadeo, Vitor M.
    Archangelo, Andreia
    Nasser, Silvia M.
    Eugenio, Rafael A. P.
    Pereira, Luiz E. R.
    Celestino, Valter R. B.
    Valarelli, Ivaldo D.
    BIORESOURCES, 2019, 14 (02) : 4590 - 4602
12345